Spectral and electrical properties of ternary (TeO2-V2O5-SM2O3)glasses

被引：93

作者：

Turky, G

Dawy, M ^{[1
]}

机构：

[1] Natl Res Ctr, Microwave Phys Dept, Cairo, Egypt

[2] Natl Res Ctr, Dept Phys Chem, Cairo, Egypt

来源：

MATERIALS CHEMISTRY AND PHYSICS | 2003年 / 77卷 / 01期

关键词：

electrical properties; spectral properties; TeO2-V2O5-Sm2O3;

D O I：

10.1016/S0254-0584(01)00574-0

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The UV and IR absorption spectra for [65TeO(2)-(35-x)V2O5-xSm(2)O(3)] glasses were measured in the ranges 190-900nm and 1004000 cm(-1), respectively, to obtain information about the structure and the effect of introducing rare earth ions as Sm. The dependence of dielectric constant, dissipation factor, dielectric loss and AC resistivity on frequency, temperature and also on the Sm amount was measured. The results obtained showed that glasses with 4 and 5 mol% Sm2O3 have higher epsilon' and epsilon" due to the weakness of the bonds. Also, the conductivity decreases till about 3 mol% and then increases with the increase of Sm2O3 due to the introduction of Sm ions in the network structure of the glass. (C) 2002 Elsevier Science B.V. All rights reserved.

引用

页码：48 / 59

页数：12

共 31 条

[1] DIELECTRIC PROPERTIES OF THIN FILMS OF ALUMINIUM OXIDE AND SILICON OXIDE [J].