Study of hydrated phases present in a MK-lime system cured at 60 °C and 60 months of reaction

被引：64
作者：
Rojas, Moises Frias [1 ]
机构：
[1] CSIC, Eduardo Torroja Inst, Madrid 28033, Spain
来源：
CEMENT AND CONCRETE RESEARCH | 2006年 / 36卷 / 05期
关键词：
metakaolin; lime; hydrated phases stability; high curing temperature; long hydration times;
D O I：
10.1016/j.cemconres.2006.01.001
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
This research presents the experimental results of a study carried out to determine the effect of curing temperature on the reaction kinetics in a metakaolin/lime mixture cured at 60 degrees C and after 60 months of hydration. The stabilities of hydrated phases formed during the pozzolanic reaction in these working conditions were evaluated. The results obtained in current paper showed that metastable hexagonal phases (C(2)ASH(8) and probably C(4)AH(13)) coexist with stable cubic phase (hydrogarnet) in the absence of lime. Also, there is evidence of the possible presence of a calcium aluminum silicate hydroxide hydrate (vertumnite). (C) 2006 Elsevier Ltd. All rights reserved.
引用
收藏
页码：827 / 831
页数：5
相关论文
共 19 条
[1]  
[Anonymous], CONCRETE 2000
[2]  
[Anonymous], 6 CANMET ACI INT C F
[3]   STRENGTH AND CHLORIDE PERMEABILITY OF CONCRETE CONTAINING RED TROPICAL SOILS [J].
CABRERA, JG ;
NWAUBANI, SO .
MAGAZINE OF CONCRETE RESEARCH, 1993, 45 (164) :169-178
[4]   PHASE-RELATIONS IN THE SYSTEM CAO-AL2O3-SIO2-H2O RELEVANT TO METAKAOLIN - CALCIUM HYDROXIDE HYDRATION [J].
DESILVA, PS ;
GLASSER, FP .
CEMENT AND CONCRETE RESEARCH, 1993, 23 (03) :627-639
[5]   THE POZZOLANIC REACTION OF METAKAOLINITE AND ITS EFFECTS ON PORTLAND-CEMENT HYDRATION [J].
DUNSTER, AM ;
PARSONAGE, JR ;
THOMAS, MJK .
JOURNAL OF MATERIALS SCIENCE, 1993, 28 (05) :1345-1350
[6]   Influence of the metakaolin on porous structure of matrixes based in mk/cement [J].
Frías, M ;
de Rojas, MIS .
MATERIALES DE CONSTRUCCION, 2000, 50 (259) :57-67
[7]   Pore size distribution and degree of hydration of metakaolin-cement pastes [J].
Frías, M ;
Cabrera, J .
CEMENT AND CONCRETE RESEARCH, 2000, 30 (04) :561-569
[8]   The effect that the pozzolanic reaction of metakaolin has on the heat evolution in metakaolin-cement mortars [J].
Frías, M ;
de Rojas, MIS ;
Cabrera, J .
CEMENT AND CONCRETE RESEARCH, 2000, 30 (02) :209-216
[9]   Total and soluble chromium, nickel and cobalt content in the main materials used in the manufacturing of Spanish commercial cements [J].
Frías, M ;
de Rojas, MIS .
CEMENT AND CONCRETE RESEARCH, 2002, 32 (03) :435-440
[10]  
FRIAS M, 2003, 11 INT C CHEM CEM DU, V2, P989
12