Tungsten Inert Gas and Friction Stir Welding Characteristics of 4-mm-Thick 2219-T87 Plates at Room Temperature and-196 A°C

被引:28
作者
Lei, Xuefeng [1 ]
Deng, Ying [1 ]
Yin, Zhimin [1 ]
Xu, Guofu [1 ]
机构
[1] Cent S Univ, Sch Mat Sci & Engn, Changsha 410083, Hunan, Peoples R China
关键词
aerospace; aluminum; electron microscopy; mechanical testing; optical microscopy; welding; MECHANICAL-PROPERTIES; FATIGUE BEHAVIOR; AGING TREATMENT; HEAT-TREATMENT; MICROSTRUCTURE; PARAMETERS; EVOLUTION;
D O I
10.1007/s11665-014-1013-9
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
2219-T87 aluminum alloy is widely used for fabricating liquid rocket propellant storage tank, due to its admirable cryogenic property. Welding is the dominant joining method in the manufacturing process of aerospace components. In this study, the tungsten inert gas welding and friction stir welding (FSW) characteristics of 4-mm-thick 2219-T87 alloy plate at room temperature (25 A degrees C) and deep cryogenic temperature (-196 A degrees C) were investigated by property measurements and microscopy methods. The studied 2219 base alloy exhibits a low strength plane anisotropy and excellent room temperature and cryogenic mechanical properties. The ultimate tensile strength values of TIG and FSW welding joints can reach 265 and 353 MPa at room temperature, and 342 and 438 MPa at -196 A degrees C, respectively. The base metal consists of elongated deformed grains and many nano-scaled theta (Al2Cu) aging precipitates. Fusion zone and heat-affected zone (HAZ) of the TIG joint are characterized by coarsening dendritic grains and equiaxed recrystallized grains, respectively. The FSW-welded joint consists of the weld nugget zone, thermo-mechanically affected zone (TMAZ), and HAZ. In the weld nugget zone, a micro-scaled sub-grain structure is the main microstructure characteristic. The TMAZ and HAZ are both characterized by coarsened aging precipitates and elongated deformed grains. The excellent FSW welding properties are attributed to the preservation of the working structures and homogenous chemical compositions.
引用
收藏
页码:2149 / 2158
页数:10
相关论文
共 17 条
[1]  
[Anonymous], 1999, P 1 INT S FRICT STIR
[2]   Microstructure Evolution during Friction Stir Welding of Aluminum Alloy AA2219 [J].
Arora, K. S. ;
Pandey, S. ;
Schaper, M. ;
Kumar, R. .
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2010, 26 (08) :747-753
[3]   The effect of post-weld heat treatment on the mechanical properties of 2024-T4 friction stir-welded joints [J].
Aydin, Hakan ;
Bayram, Ali ;
Durgun, Ismail .
MATERIALS & DESIGN, 2010, 31 (05) :2568-2577
[4]  
Dalle Donne C., 2001, 3 INT S FRICT STIR W
[5]   Analysis of microstructural evolution during friction stir welding of ultrahigh-strength steel [J].
Ghosh, M. ;
Kumar, K. ;
Mishra, R. S. .
SCRIPTA MATERIALIA, 2010, 63 (08) :851-854
[6]   The effect of welding parameters on the corrosion behaviour of friction stir welded AA2024-T351 [J].
Jariyaboon, M. ;
Davenport, A. J. ;
Ambat, R. ;
Connolly, B. J. ;
Williams, S. W. ;
Price, D. A. .
CORROSION SCIENCE, 2007, 49 (02) :877-909
[7]   Liquation cracking of Al-6.3 Cu alloy propellant storage tank - A case study [J].
Jha, Abhay K. ;
Narayanan, P. Ramesh ;
Sreekumar, K. .
ENGINEERING FAILURE ANALYSIS, 2009, 16 (05) :1587-1596
[8]   Minimization of residual stress in heat-treated Al-Si-Mg cast alloys using uphill quenching: Mechanisms and effects on static and dynamic properties [J].
Lados, Diana A. ;
Apelian, Diran ;
Wang, Libo .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (13-14) :3159-3165
[9]   Fatigue behaviour of post weld heat treated electron beam welded AA2219 aluminium. alloy joints [J].
Malarvizhi, S. ;
Raghukandan, K. ;
Viswanathan, N. .
MATERIALS & DESIGN, 2008, 29 (08) :1562-1567
[10]   Investigations on the influence of post weld heat treatment on fatigue crack growth behaviour of electron beam welded AA2219 alloy [J].
Malarvizhi, S. ;
Raghukandan, K. ;
Viswanathan, N. .
INTERNATIONAL JOURNAL OF FATIGUE, 2008, 30 (09) :1543-1555