Flexural properties evaluation of carbon-fiber fabric reinforced poplar/eucalyptus composite plywood formwork

被引:25
作者
Liu, Yuansong [1 ,2 ]
Guan, Mingjie [1 ]
Chen, Xianwen [1 ]
Zhang, Yuan [1 ]
Zhou, Mingming [3 ]
机构
[1] Nanjing Forestry Univ, Coll Mat Sci & Engn, Nanjing 210037, Jiangsu, Peoples R China
[2] Beijing Forestry Univ, Coll Mat Sci & Engn, Beijing 100089, Peoples R China
[3] CNIPA, Patent Examinat Cooperat Jiangsu Ctr Paternt Off, Beijing 215000, Peoples R China
关键词
Building formwork; CF fabric; Plywood; Composites; Failure model; PLANNING-MODEL; FRESH CONCRETE; WOOD; PRESSURE; DESIGN; BEAMS;
D O I
10.1016/j.compstruct.2019.111073
中图分类号
O3 [力学];
学科分类号
08 ; 0801 ;
摘要
To improve the product quality of traditional wooden building formwork, utilize the resources of wood and evaluate the failure mode of the formwork. Carbon-fiber fabric (CF fabric) reinforced poplar/eucalyptus composite plywood were prepared by using fast-growing poplar (P) and eucalyptus (E) veneer as base materials and CF fabric as reinforcement material, four substrate composite structures (P/P, E/E, P/E, E/P) and four reinforcement positions (control/A, surface/B, core/C and surface-core/D) were considered in this study, the flexural properties and failure modes of plywood were tested and evaluated. Experimental results showed that the flexural performance of plywood as poplar/eucalyptus composite structure was better than pure poplar and eucalyptus. The increase in the longitudinal modulus of elasticity and modulus of rupture of the plywood was particularly understandable and the failure mode was shear delamination failure after the surface strengthened, besides, the core layer reinforced transverse plywood was greater obvious than the longitudinal plywood for the improvement in impact toughness. However, the plywood strengthened by the surface and core simultaneously had the best performance, and the structure which satisfies the strength requirements of building formwork are D-P/E and D-E/P. Experimental findings are accompanied with theoretical model.
引用
收藏
页数:8
相关论文
共 50 条
[31]   Thermal, Mechanical and Electrical Properties of Carbon Fiber Fabric and Graphene Reinforced Segmented Polyurethane Composites [J].
Shi, Zhe ;
Zhang, Cong ;
Chen, Xin-Gang ;
Li, Ang ;
Zhang, Yang-Fei .
NANOMATERIALS, 2021, 11 (05)
[32]   Voids Formation and Their Effects on Mechanical Properties in Thermoformed Carbon Fiber Fabric-Reinforced Composites [J].
Jiang, Wei ;
Huang, Zhigao ;
Wang, Yunming ;
Zheng, Bing ;
Zhou, Huamin .
POLYMER COMPOSITES, 2019, 40 (S2) :E1094-E1102
[33]   Properties Variation of Carbon Fiber Reinforced Composite for Marine Current Turbine in Seawater [J].
Li Jing ;
Hou Shipu ;
Zhao Peng ;
Jia Penggang ;
Ge Guangnan ;
Liu Yuxin ;
Wen Daowei ;
Li Zheng .
INTERNATIONAL SYMPOSIUM ON MATERIALS APPLICATION AND ENGINEERING (SMAE 2016), 2016, 67
[34]   Grass fiber reinforced phenol formaldehyde resin composite: preparation, characterization and evaluation of properties of composite [J].
De, Debasish ;
Adhikari, Basudam ;
De, Debapriya .
POLYMERS FOR ADVANCED TECHNOLOGIES, 2007, 18 (01) :72-81
[35]   Improving the tensile and flexural properties of reinforced epoxy composites by using cobalt filled and carbon/glass fiber [J].
Rajak, Dipen Kumar ;
Wagh, Pratiksha H. ;
Moustabchir, Hassan ;
Pruncu, Catalin I. .
FORCES IN MECHANICS, 2021, 4
[36]   Effect of fiber hybridization types on the mechanical properties of carbon/glass fiber reinforced polymer composite rod [J].
Guo, Rui ;
Xian, Guijun ;
Li, Chenggao ;
Huang, Xiangyu ;
Xin, Meiyin .
MECHANICS OF ADVANCED MATERIALS AND STRUCTURES, 2022, 29 (27) :6288-6300
[37]   Microstructure and Mechanical Properties of SiC and Carbon Hybrid Fiber Reinforced SiC Matrix Composite [J].
Liu, Shanhua ;
Zhang, Litong ;
Yin, Xiaowei ;
Cheng, Laifei ;
Liu, Yongsheng .
INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2011, 8 (02) :308-316
[38]   Rehabilitation and strength sustainability of fatigue damaged concrete-encased steel flexural members using a newly developed polymeric carbon-fiber composite [J].
Zhou, Hongyu ;
Attard, Thomas L. .
COMPOSITES PART B-ENGINEERING, 2013, 45 (01) :1091-1103
[39]   The impact of prepreg aging on its processability and the postcure mechanical properties of epoxy-based carbon-fiber reinforced plastics [J].
Blass, D. ;
Kreling, S. ;
Dilger, K. .
PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART L-JOURNAL OF MATERIALS-DESIGN AND APPLICATIONS, 2017, 231 (1-2) :62-72
[40]   Effects of molecular weight on the dynamic mechanical properties and interfacial properties of carbon fiber fabric-reinforced polyetherketone cardo composites [J].
Ma, Yan ;
Bi, Ying ;
Zhang, Xingdi ;
Wang, Daming ;
Dang, Guodong ;
Zhou, Hongwei ;
Chen, Chunhai .
HIGH PERFORMANCE POLYMERS, 2016, 28 (10) :1210-1217