Role of grain size on the stress corrosion cracking of 7475 aluminum alloys

被引：113
作者：
Tsai, TC [1 ]
Chuang, TH [1 ]
机构：
[1] NATL TAIWAN UNIV,INST MAT SCI & ENGN,TAIPEI 10764,TAIWAN
来源：
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 1997年 / 225卷 / 1-2期
关键词：
grain refinement; grain boundary precipitates; stress corrosion cracking; hydrogen embrittlement;
D O I：
10.1016/S0921-5093(96)10840-6
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The effect of grain size upon the stress corrosion cracking of 7475 Al-alloy plates has been investigated. Grain refinement resulted in a more homogeneous slip mode and a smaller size of grain boundary precipitates (GBPs) to influence the stress corrosion cracking (SCC) resistance. The more homogeneous slip mode is always beneficial for improving the SCC resistance. However, if the GBPs size was smaller than a critical precipitate size for nucleating hydrogen bubbles, the improvement of SCC resistance due to grain refinement, resulting from a more homogeneous slip mode, could not be obtained. The correlation of SCC susceptibility and hydrogen embrittlement susceptibility has been evaluated. The SCC susceptibility of the 7475 aluminum alloys is mainly controlled by hydrogen induced cracking mechanism. (C) 1997 Elsevier Science S.A.
引用
收藏
页码：135 / 144
页数：10
相关论文
共 25 条
[1]   INFLUENCE OF MICROSTRUCTURE ON MECHANICAL PROPERTIES AND STRESS-CORROSION SUSCEPTIBILITY OF 7075 ALUMINUM-ALLOY [J].
ADLER, PN ;
DEIASI, R ;
GESCHWIND, G .
METALLURGICAL TRANSACTIONS, 1972, 3 (12) :3191-3200
[2]   EVIDENCE FOR DISLOCATION TRANSPORT OF HYDROGEN IN ALUMINUM [J].
ALBRECHT, J ;
BERNSTEIN, IM ;
THOMPSON, AW .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (05) :811-820
[3]   INDUSTRIAL-ASPECTS OF SUPERPLASTICITY [J].
BAUDELET, B .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 137 :41-55
[4]   EVALUATION OF THE STRESS-CORROSION CRACKING BEHAVIOR OF DAMAGE-TOLERANT AL-LI SHEET USING THE SLOW STRAIN-RATE TESTING TECHNIQUE [J].
BRAUN, R .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 190 (1-2) :143-154
[5]   THE POSTULATED MECHANISMS FOR STRESS-CORROSION CRACKING OF ALUMINUM-ALLOYS - A REVIEW OF THE LITERATURE 1980-1989 [J].
BURLEIGH, TD .
CORROSION, 1991, 47 (02) :89-98
[6]   HYDROGEN EMBRITTLEMENT AND TRAPPING IN AL-6-PERCENT-ZN-3-PERCENT-MG [J].
CHRISTODOULOU, L ;
FLOWER, HM .
ACTA METALLURGICA, 1980, 28 (04) :481-487
[7]  
Cina B, 1974, Patent No. 3856584
[8]  
Gruhl W., 1978, Aluminium, V54, P323
[9]  
HAMILTON CH, 1989, SUPERPLSTICITY SUPER
[10]  
HAMILTON CH, 1989, SUPERPLASTICITY SUPE
123