Development and characterization of sol-gel silica-alumina composite coatings on AISI 316L for implant applications

被引：79

作者：

Tiwari, S. K. ^{[1
]}

Mishra, T. ^{[1
]}

Gunjan, M. K. ^{[1
]}

Bhattacharyya, A. S. ^{[1
]}

Singh, T. B. ^{[1
]}

Singh, R. ^{[1
]}

机构：

[1] Natl Met Lab, Jamshedpur 831007, Bihar, India

来源：

SURFACE & COATINGS TECHNOLOGY | 2007年 / 201卷 / 16-17期

关键词：

stainless steel; coating; sol-gel; aluminium oxide; corrosion resistance; bioimplant;

D O I：

10.1016/j.surfcoat.2007.02.026

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Sol-gel alumina coatings were deposited on medical grade stainless steel (AISI 316L) with an intermediate layer of silica by dip-coating method. The coatings obtained were homogeneous, crack-free and consisted of low crystalline gamma-Al2O3 along with some boehmite phase. EDAX revealed the presence of only Al in the film. The corrosion performance of alumina-coated stainless steel was evaluated by electrochemical polarization, open-circuit potential measurement and chronoamperometry in Ringer's solution. Coating has shown to enhance the pitting potential of AISI 316L by similar to 470 mV and reduced passive current <= 10(-9) A cm(-2). The formation of thermodynamically stable silica-alumina interface was proposed to account for enhanced corrosion protection behaviour of the coating. (C) 2007 Elsevier B.V. All rights reserved.