Influence of implant surface topography on bone-regenerative potential and mechanical retention in the human maxilla and mandible

Purpose: To evaluate the short- and mid-term effects of commercial pure (cp) titanium implant surface topography on osseointegration, bone-regenerative potential and mechanical retention in the human maxilla and mandible. Methods: 32 micro-implants with the same geometry but with four different surface treatments were implanted in the maxilla and mandible of eight patients. Each patient received four micro-implants, one of each type. Percentage of bone-to-implant contact analysis and histological evaluation was carried 3, 6 and 12 weeks after implantation. Furthermore, reverse removal torque tests were conducted 3 and 6 weeks after implantation to analyze functional bone attachment. Implant surfaces tested were machined, grit-blasted, acid-etched, and grit-blasted with acid-etch. One-way ANOVA was performed using the multiple comparison Fisher's test to determine significance of observed differences among test groups. The level of significance was established at 5% (P< 0.05). Mean and standard deviations of the test groups were calculated. Results: Surface roughness had a significant correlation with the evolution of bone regeneration. The surfaces with roughness Ra approximate to 4 mu m (grit-blasted and grit-blasted with acid-etch), showed rapid tissue colonization compared to machine and acid-etched surfaces. The results of reverse removal torque tests confirmed a significant correlation between surface roughness and functional bone attachment. Grit-blasted and grit-blasted with acid etched surfaces showed higher retention values compared to machine and acid-etched implants. This finding was supported by higher bone-to-implant contact observed for rougher surfaces (grit-blasted and grit-blasted with acid etching).