Morphology and characterization studies of Y doped Bi-2212 single crystals

被引：3
作者：
Prabhakaran, D
Thamizhavel, A
Subramanian, C
机构：
[1] Crystal Growth Centre, Anna University, Madras
来源：
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS | 1997年 / 288卷 / 3-4期
关键词：
D O I：
10.1016/S0921-4534(97)01591-8
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
Superconducting Bi-2212 single crystals of nominal composition Bi2.2Sr1.9CaCu2O8, B2.1Y0.1Sr1.9CaCu2O8 and Bi2.2Sr1.9Ca0.9Y0.1Cu2O8 have been grown by flux method using a conical shaped Al2O3 crucible. Effect of Y doping on the crystal morphology has been studied. From the X-ray diffraction studies, the cell parameters were calculated. AC susceptibility showed that Y doping gives rise to highest T-c,T-onset at 92 K and the effect of annealing was also studied. The crystal composition at different places of the crucible and the Al incorporation were studied. The Sr/Ca ratio has been correlated with Y substitution. Chemical etching was also carried out on the grown crystals in order to reveal the nature of twinning and dislocations. (C) 1997 Elsevier Science B.V.
引用
收藏
页码：249 / 254
页数：6
相关论文
共 50 条
[41]   Influences of Yb Doping on the Structure and Superconducting Properties of Bi-2212 Single Crystals [J].
Lu, Tian-Ni ;
Zhang, Cui-Ping ;
Guo, Sheng-Wu ;
Wu, Yi-Fang ;
Li, Cheng-Shan ;
Zhou, Lian .
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2015, 25 (04)
[42]   Improvement of superconductivity in Bi-2212 single crystals grown by a vertical Bridgman method [J].
Nagashima, O ;
Tanaka, H ;
Ebara, Y ;
Kishida, S .
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2003, 392 :505-507
[43]   MAGNETIC MEASUREMENTS ON TL-2212 AND BI-2212 SINGLE-CRYSTALS - A COMPARATIVE-STUDY [J].
OUSSENA, M ;
PORTER, S ;
VOLKOZUB, A ;
DEGROOT, PAJ ;
LANCHESTER, PC ;
OGBORNE, D ;
WELLER, MT ;
BALAKRISHNAN, G ;
PAUL, DM .
PHYSICA B-CONDENSED MATTER, 1994, 194 :1885-1886
[44]   IRREVERSIBILITY LINES OF YB AND PB SUBSTITUTED BI-2212 SINGLE-CRYSTALS [J].
RUYTER, A ;
SIMON, C ;
HARDY, V ;
HERVIEU, M ;
MAIGNAN, A .
PHYSICA C, 1994, 225 (3-4) :235-239
[45]   INFRARED REFLECTIVITY OF BI-2212 SINGLE-CRYSTALS WITH DIFFERENT OXYGEN STOICHIOMETRIES [J].
PRENNINGER, M ;
PRUCKL, A ;
RENK, KF ;
BUCKLEY, RG ;
POOKE, DM ;
KISHIO, K .
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 1994, 235 :1131-1132
[46]   Growth of Bi-2212 single crystals by the travelling solvent zone melting method [J].
Tanaka, I ;
Iwamoto, T ;
Islam, ATMN ;
Watauchi, S .
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2002, 15 (03) :458-461
[47]   Evaluation of anisotropy of critical current density in stoichiometric Bi-2212 single crystals [J].
Nakayama, Y. ;
Kawai, S. ;
Kiuchi, M. ;
Otabe, E. S. ;
Matsushita, T. ;
Shimoyama, J. ;
Kishio, K. .
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2009, 469 (15-20) :1221-1223
[48]   Contamination by alumina crucible and the effect of Al on Tc for Bi-2212 single crystals [J].
He, YZ ;
Zhou, F ;
Zhao, ZX .
PHYSICA C, 1999, 328 (3-4) :207-210
[49]   MAGNETORESISTANCE IN BI-2212 SINGLE-CRYSTAL [J].
SORET, JC ;
AMMOR, L ;
MARTINIE, B ;
GOUPIL, C ;
HARDY, V ;
PROVOST, J ;
RUYTER, A ;
SIMON, C .
PHYSICA C, 1994, 220 (3-4) :242-248
[50]   Thermal conductivity of Ce doped Bi-2212 superconductors [J].
Li, B ;
Wu, BM ;
Ausloos, M .
CHINESE PHYSICS LETTERS, 2004, 21 (07) :1337-1339
12345