Morphology and characterization studies of Y doped Bi-2212 single crystals

被引：3
作者：
Prabhakaran, D
Thamizhavel, A
Subramanian, C
机构：
[1] Crystal Growth Centre, Anna University, Madras
来源：
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS | 1997年 / 288卷 / 3-4期
关键词：
D O I：
10.1016/S0921-4534(97)01591-8
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
Superconducting Bi-2212 single crystals of nominal composition Bi2.2Sr1.9CaCu2O8, B2.1Y0.1Sr1.9CaCu2O8 and Bi2.2Sr1.9Ca0.9Y0.1Cu2O8 have been grown by flux method using a conical shaped Al2O3 crucible. Effect of Y doping on the crystal morphology has been studied. From the X-ray diffraction studies, the cell parameters were calculated. AC susceptibility showed that Y doping gives rise to highest T-c,T-onset at 92 K and the effect of annealing was also studied. The crystal composition at different places of the crucible and the Al incorporation were studied. The Sr/Ca ratio has been correlated with Y substitution. Chemical etching was also carried out on the grown crystals in order to reveal the nature of twinning and dislocations. (C) 1997 Elsevier Science B.V.
引用
收藏
页码：249 / 254
页数：6
相关论文
共 50 条
[31]   EFFECT OF PRESSURE ON THE IRREVERSIBILITY LINE IN BI-2212 SINGLE-CRYSTALS [J].
BUDKO, SL ;
LUPPOV, AE ;
GAPOTCHENKO, AG ;
MOTOHIRA, N .
SOLID STATE COMMUNICATIONS, 1995, 96 (04) :189-193
[32]   Correlation between modulation structure and electronic inhomogeneity on Pb-doped Bi-2212 single crystals [J].
Sugimoto, A ;
Kashiwaya, S ;
Eisaki, H ;
Yamaguchi, H ;
Oka, K ;
Kashiwaya, H ;
Tsuchiura, H ;
Tanaka, Y .
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2005, 426 :390-395
[33]   Electromechanical Characterization of Bi-2212 Strands [J].
Lu, X. F. ;
Cheggour, N. ;
Stauffer, T. C. ;
Clickner, C. C. ;
Goodrich, L. F. ;
Trociewitz, U. ;
Myers, D. ;
Holesinger, T. G. .
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2011, 21 (03) :3086-3089
[34]   THE EFFECT OF ANNEALING ON THE SUPERCONDUCTING PROPERTIES AND STRUCTURE OF BI-2212 SINGLE-CRYSTALS [J].
HAN, SH ;
GU, GD ;
SHAO, Y ;
RUSSELL, GJ ;
KOSHIZUKA, N .
PHYSICA C, 1995, 246 (1-2) :22-28
[35]   OPTICALLY INDUCED MAGNETIC-RELAXATION IN BI-2212 SINGLE-CRYSTALS [J].
YURGENS, AA ;
ZAVARITSKY, NV .
PHYSICA C, 1992, 203 (3-4) :277-283
[36]   Driven depinning of vortices in irradiated microbridge single-crystals of Bi-2212 [J].
Ruyter, A ;
Pignon, B ;
Plessis, D ;
Topart, P ;
Plain, J ;
Simon, C ;
Pautrat, A ;
Maignan, A ;
Ammor, L .
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 2006, 67 (1-3) :468-471
[37]   Second step in the field-cooled magnetization of Bi-2212 single crystals [J].
Koblischka, MR ;
Murakami, M .
PHYSICA STATUS SOLIDI B-BASIC RESEARCH, 2000, 218 (01) :R3-R5
[38]   Annealing experiment on high-Tc superconductor Bi-2212 single crystals [J].
Gu, GD ;
Han, SH ;
Lin, ZW ;
Zhao, Y ;
Russell, GJ .
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1998, 11 (10) :1118-1122
[39]   Interplay between two families of columnar defects in Bi-2212 single crystals [J].
Hébert, S ;
Perkins, G ;
Abd el-Salam, M ;
Caplin, AD .
PHYSICA C, 2000, 341 :1237-1238
[40]   On the growth of overdoped Bi-2212 single crystals under high oxygen pressure [J].
Maljuk, A ;
Liang, B ;
Lin, CT ;
Emelchenko, GA .
PHYSICA C, 2001, 355 (1-2) :140-146
12345