Influence of Ti ions valence states on the optical and magnetic properties of GdCr1-xTixO3 (0≤x≤0.05)

The vacancy defects, optical and magnetic properties of GdCr1-xTixO3 (0 <= x <= 0.05) polycrystalline samples were investigated in this research. The crystal structural analyses show that the orthorhombic perovskite structure exists in all the samples. The positron annihilation spectra reveal that the vacancy defects and local electron density vary with the change of Ti ions valence states. The magnetic measurements show that the antiferromagnetic transition is shifted to lower temperature with the replacement of Ti ions in Cr sites, and the value of spin reorientation caused by the exchange interaction between Gd3+ ion and Cr3+ ion can be influenced by the change of Ti ions valence states, which rises from x = 0 to 0.04 and then decreases at x = 0.05 sample. Simultaneously, the optical band gap decreases from 2.7 eV to 0.8 eV with the introduction of Ti ions into the lattice, the result can provide a reference for improving optical activity of rare-earth chromium oxides.