Influence of Chloride on Passive Film Chemistry of 304 Stainless Steel in Sulphuric Acid Solution by Glow Discharge Optical Emission Spectrometry Analysis

被引：18

作者：

Deng, Saifu ^{[1
]}

Wang, Shuangbao ^{[1
]}

Wang, Linyue ^{[1
]}

Liu, Jianting ^{[1
]}

Wang, Yujie ^{[1
]}

机构：

[1] Huazhong Univ Sci & Technol, Sch Opt & Elect Informat, Wuhan 430074, Peoples R China

来源：

INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE | 2017年 / 12卷 / 02期

关键词：

304 stainless steel; GD-OES; passive film; pitting corrosion; AUSTENITIC STAINLESS-STEEL; NACL SOLUTION; PITTING CORROSION; 3.5-PERCENT NACL; CURRENT-DENSITY; PURE ALUMINUM; SO42-IONS; CL-IONS; 316L SS; BEHAVIOR;

D O I：

10.20964/2017.02.43

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

The influence of chloride on passive film formed on 304 stainless steels (SS) in 0.2 M H2SO4 solution has been investigated by potentiostatic polarization experiments and glow discharge optical emission spectroscopy (GD-OES) analysis. Chromium was enriched in outer and inner layers of passive film after potentiostatic passivation. The Cr/Fe ratio of the passive film increased with immersion time of passivation, which suggested the improvement of corrosion resistance. The breakdown of passivity was evaluated by addition of sodium chloride (NaCl). Pitting corrosion appeared on the surface of the passive film when 3 wt% of NaCl was added into the solution, thereby resulting in a decrease of iron species in the outer layer of the passive film. The depth profiles showed the appearance of chlorine in the passive film region of 304 SS polarized in chloride-containing solution. The decrease of Cl species intensity from the outer layer to the inner layer validated the penetration of chloride ions through passive film during pitting corrosion.

引用

页码：1106 / 1117

页数：12

共 42 条

[1] High frequency impedance spectroscopy study of passive films formed on AISI 316 stainless steel in alkaline medium [J].

Abreu, CM ;

Cristóbal, MJ ;

Losada, R ;

Nóvoa, XR ;

Pena, G ;

Pérez, MC .

JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2004, 572 (02) :335-345

[2] TOF-SIMS study on surface modification of reed switch blades by pulsing nitrogen plasma [J].

Arushanov, K. A. ;

Drozdov, M. N. ;

Karabanov, S. M. ;

Zeltser, I. A. ;

Tolstogouzov, A. .

APPLIED SURFACE SCIENCE, 2013, 265 :642-647

[3] CORROSION OF STAINLESS-STEELS IN CHLORIDE SOLUTION - AN XPS INVESTIGATION OF PASSIVE FILMS [J].

BRUESCH, P ;

MULLER, K ;

ATRENS, A ;

NEFF, H .

APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 1985, 38 (01) :1-18

[4]

Cabral-Miramontes JA, 2013, INT J ELECTROCHEM SC, V8, P564

[5] THE EFFECT OF THE CL- ION ON THE PASSIVE FILM ON ANODICALLY POLARIZED 304 STAINLESS-STEEL [J].

CURLEYFIORINO, ME ;

SCHMID, GM .

CORROSION SCIENCE, 1980, 20 (03) :313-329

[6] Hydrogen absorption associated with the corrosion mechanism of 316L stainless steels in primary medium of Pressurized Water Reactor (PWR) [J].

Dumerval, Marie ;

Perrin, Stephane ;

Marchetti, Loic ;

Tabarant, Michel ;

Jomard, Francois ;

Wouters, Yves .

CORROSION SCIENCE, 2014, 85 :251-257

[7]

Ericson S., 2013, INT J ELECTROCHEM SC, V8, P5851

[8] Pitting corrosion of metals - A review of the critical factors [J].

Frankel, GS .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1998, 145 (06) :2186-2198

[9] Effects of cyclic stress on the metastable pitting characteristic for 304 stainless steel under potentiostatic polarization [J].

Guan, L. ;

Zhang, B. ;

Yong, X. P. ;

Wang, J. Q. ;

Han, E. -H. ;

Ke, W. .

CORROSION SCIENCE, 2015, 93 :80-89

[10] Analytical and numerical depth resolution functions in sputter profiling [J].

Hofmann, S. ;

Liu, Y. ;

Wang, J. Y. ;

Kovac, J. .

APPLIED SURFACE SCIENCE, 2014, 314 :942-955

← 1 2 3 4 5 →