PREPARATION OF Al-Sc MASTER ALLOY BY ALUMINOTHERMIC REACTION WITH SPECIAL MOLTEN SALT

被引：0

作者：

Xu, Cong ^{[1
]}

Liu, Xinxin ^{[1
]}

Ma, Fengmei ^{[1
]}

Wang, Zhiwei ^{[1
]}

Wang, Wenhong ^{[2
]}

Ma, Chaoli ^{[1
]}

机构：

[1] Beihang Univ, Sch Mat Sci & Engn, Minist Educ, Key Lab Aerosp Adv Mat & Performance, Beijing, Peoples R China

[2] Hebei Sitong New Met Mat Co Ltd, Baoding, Peoples R China

来源：

PROCEEDINGS OF THE 13TH INTERNATIONAL CONFERENCE ON ALUMINUM ALLOYS (ICAA13) | 2012年

关键词：

Al-Sc master alloy; special molten salt; aluminothermic reaction; residue; SCANDIUM;

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Al-Sc master alloy is prepared by aluminothermic reaction with a kind of special molten salt under the normal atmospheric condition. To achieve larger Sc recovery rate, the composition and pretreatment of the molten salt are studied. The optimum molten salt is obtained by melting together Sc2O3, NaF, KCl, NaCl, ScF3 and Na3AlF6 mixture under a mass ratio of 3:5:10:10:2:30, followed by solidifying and crushing. The pretreated salt is added to the Aluminum melt with a mass ratio of 60:100 to prepare Al-Sc master alloy. When the residue of molten salt is reused for three times, the Sc recovery rate can reach 91%. The structure and composition of the residue are examined using X-ray diffraction (XRD) analyzer and differential scanning calorimetry (DSC) analyzer. Based on the analysis of the residue, mechanism of the aluminothermic reaction to achieve larger Sc recovery rate with this special molten salt is discussed.

引用

页码：195 / 200

页数：6

共 14 条

[1]

Danek V., 2006, PHYSICOCHEMICAL ANAL

[2]

Danilov S. F., 1992, P 6 INT C AL LI ALL, P381

[3] Scientific principles of making an alloying addition of scandium to aluminium alloys [J].

Davydov, VG ;

Rostova, TD ;

Zakharov, VV ;

Filatov, YA ;

Yelagin, VI .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 280 (01) :30-36

[4] Grain refinement of aluminum alloys: Part I. The nucleant and salute paradigms - A review of the literature [J].

Easton, M ;

StJohn, D .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (06) :1613-1623

[5]

Kramer LS, 1997, ADV MATER PROCESS, V152, P23

[6]

Liu X. S, 1999, CHINESE J NONFERROUS, V9, P171

[7]

MURTY BS, 2002, INT MATER REV, V18, P2

[8] The solidification behaviour of dilute aluminium-scandium alloys [J].

Norman, AF ;

Prangnell, PB ;

McEwen, RS .

ACTA MATERIALIA, 1998, 46 (16) :5715-5732

[9]

Pa LAWLB, 1971, Patent No. [US3619181A, 3619181]

[10] On the phase diagram of the binary system Sc2O3-ScF3 in the temperature range 1400-1840 K [J].

Petzel, T ;

Schneider, F ;

Hormann, B .

THERMOCHIMICA ACTA, 1996, 276 :1-6

← 1 2 →