Numerical investigation on stress concentration of corrosion pit

被引：287

作者：

Cerit, M. ^{[1
]}

Genel, K. ^{[1
]}

Eksi, S. ^{[1
]}

机构：

[1] Sakarya Univ, Dept Mech Engn, TR-54187 Adapazari, Turkey

来源：

ENGINEERING FAILURE ANALYSIS | 2009年 / 16卷 / 07期

关键词：

Pitting corrosion; Stress concentrations; Finite element analysis; Fatigue crack; Structural failures; FATIGUE-CRACK INITIATION; ALUMINUM-ALLOY; BEHAVIOR;

D O I：

10.1016/j.engfailanal.2009.04.004

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Localized (pitting) corrosion has been observed in steel and high-strength aluminium alloys in aqueous environments and has been identified as a potential origin for fatigue crack nucleation. In the present study, under uniaxial tension loading, stress distribution at the semi-elliptical corrosion pits has been investigated by conducting a series of three-dimensional semi-elliptical pitted models, systematically. Based on the finite element analyses, it is concluded that pit aspect ratio (a/2c) is a main parameter affecting stress concentration factor (SCF). An attempt has been made to construct simple equations to SCIF depending on characteristic of pit parameters. At the bottom of hemispherical pit, contribution of secondary (premature) pit formation to SCF is very pronounced. (C) 2009 Elsevier Ltd. All rights reserved.

引用

页码：2467 / 2472

页数：6

共 50 条

[41] 3D analysis for pit evolution and pit-to-crack transition during corrosion fatigue [J].

Huang, Xiao-guang ;

Xu, Jin-quan .

JOURNAL OF ZHEJIANG UNIVERSITY-SCIENCE A, 2013, 14 (04) :292-299

[42] Numerical Investigation of the Role of Volumetric Transformation Strain on the Relaxation Stress and the Corresponding Hydrogen Interstitial Concentration in Niobium Matrix [J].

Bal, Burak .

ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2017, 2017

[43] Rate of Reinforcement Corrosion and Stress Concentration in Concrete Columns Repaired with Bonded and Unbonded FRP Wraps [J].

Nossoni, G. ;

Harichandran, R. S. ;

Baiyasi, M. I. .

JOURNAL OF COMPOSITES FOR CONSTRUCTION, 2015, 19 (05)

[44] Impact of strain on the corrosion resistance of 304 stainless steel welded joints using electrochemical methods and numerical modeling of stress corrosion [J].

Tang, Ziqin ;

Wang, Bingbing ;

Aday, Xieeryazidan .

INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2025, 20 (01)

[45] Investigation of cable bolts for stress corrosion cracking failure [J].

Wu, Saisai ;

Chen, Honghao ;

Ramandi, Flamed Lamei ;

Hagan, Paul C. ;

Hebblewhite, Bruce ;

Crosky, Alan ;

Saydam, Serkan .

CONSTRUCTION AND BUILDING MATERIALS, 2018, 187 :1224-1231

[46] Fatigue crack propagation near a corrosion pit in a HSS specimen [J].

Malikova, Lucie ;

Miarka, Petr .

THEORETICAL AND APPLIED FRACTURE MECHANICS, 2024, 129

[47] On the Modeling of Wave Phenomena in Pit Corrosion [J].

Pollino, Annamaria .

RICERCHE DI MATEMATICA, 2025,

[48] Hydrodynamic measurement of a single corrosion pit [J].

Volkov, AV ;

Datta, PK ;

Burnell-Gray, JS ;

Couper, R .

CORROSION SCIENCE, 2004, 46 (11) :2613-2619

[49] Numerical Simulation of Micro-Galvanic Corrosion in Al Alloys: Steric Hindrance Effect of Corrosion Product [J].

Wang, Yongchao ;

Yin, Litao ;

Jin, Ying ;

Pan, Jinshan ;

Leygraf, Christofer .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2017, 164 (14) :C1035-C1043

[50] Numerical modeling of corrosion pit propagation using the combined extended finite element and level set method [J].

Ravindra Duddu .

Computational Mechanics, 2014, 54 :613-627

← 1 2 3 4 5 →