Microstructural characterization of GPSed-RBSN and GPSed-Si3N4 ceramics

被引：17
|
作者：
Lee, BT
Yoo, JH
Kim, HD
机构：
[1] Kongju Natl Univ, Div Adv Mat Engn, Kongju 314701, South Korea
[2] Korea Inst Machinery & Mat, Ceram Mat Grp, Changwon 641010, South Korea
来源：
MATERIALS TRANSACTIONS JIM | 2000年 / 41卷 / 02期
关键词：
microstructure; gas-pressure-sintering; reaction-bonded silicon nitride; fracture toughening mechanism;
D O I：
10.2320/matertrans1989.41.312
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Microstructural characterization of gas-pressure-sintered reaction-bonded Si3N4 (GPSed RBSN) and gas pressure-sintered Si3N4 (GPSed Si3N4) ceramics at 2223 K far 12.6 ks has been investigated using by back-scattered SEM, TEM and XRD. No residual Si phase was observed in reaction bonded body nitrided at 1673 K for 72 ks, but many residual pores with about 3 mu m was observed. Most of Si3N4 grain boundaries and triple points in both GPSed bodies were covered with amorphous phases. The aspect ratio of large rod-like Si3N4 grains in GPSed Si3N4 was about 10, which was larger than that in GPSed RBSN body. The main fracture mode in both sintered bodies was intergranular fracture with rough surfaces. The values of fracture toughness and fracture strength in both samples were 7.8 MPa.m(1/2), 731 MPa and. 8.0 MPa.m(1/2). 632 MPa, respectively.
引用
收藏
页码：312 / 316
页数：5
相关论文
共 50 条
  • [41] Grain boundary character distributions in Si3N4 ceramics
    Zhao Ming-Liang
    Chen Song
    Sun Feng
    Zhang Jing
    Lin Yan
    Zhang Wei-Ru
    Wang Wei-Guo
    ACTA PHYSICA SINICA, 2021, 70 (22)
  • [42] Mechanical and electromagnetic shielding properties of colored Si 3 N 4 ceramics
    Xu, Zhenru
    Zhu, Xiaotong
    Zhang, Shuai
    Li, Tongyang
    Qiao, Zhuhui
    CERAMICS INTERNATIONAL, 2024, 50 (17) : 29282 - 29292
  • [43] Preparation and characterization of porous Si3N4 ceramics prepared by compression molding and slip casting methods
    Fangli Yu
    Huanrui Wang
    Yu Bai
    Jianfeng Yang
    Bulletin of Materials Science, 2010, 33 : 619 - 624
  • [44] Preparation and characterization of porous Si3N4 ceramics prepared by compression molding and slip casting methods
    Yu Fangli
    Wang Huanrui
    Bai Yu
    Yang Jianfeng
    BULLETIN OF MATERIALS SCIENCE, 2010, 33 (05) : 619 - 624
  • [45] Lightweight, high-strength, and broadband transmission porous Si3N4 3 N 4 ceramics
    Ye, Jian
    Zhang, Biao
    Ren, Yuhan
    Zhong, Zhaoxin
    Wang, Yujin
    Ye, Feng
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2024, 44 (15)
  • [46] Improved mechanical properties of porous Si3N4 ceramics strengthened by (3-Si 3 N 4 seeds fabricated by vat photopolymerization
    Mao, Guang-Xin
    Wu, Jia-Min
    Tian, Chong
    Liu, Chun-Lei
    Lin, Xin
    Wang, Fen
    Xu, Hai-Sheng
    Shi, Yu-Sheng
    CERAMICS INTERNATIONAL, 2024, 50 (23) : 49058 - 49065
  • [47] Preparation of porous Si3N4 ceramics via tailoring solid loading of Si3N4 slurry and Si3N4 poly-hollow microsphere content
    Wu, Jia-Min
    Zhang, Xiao-Yan
    Xu, Jie
    Gan, Ke
    Li, Jia-Lu
    Li, Chen-Hui
    Yang, Jin-Long
    Shi, Yu-Sheng
    JOURNAL OF ADVANCED CERAMICS, 2015, 4 (04) : 260 - 266
  • [48] Optimization of microstructure to improve Si3N4 ceramics with thermal conductivity and mechanical properties: Effect of Si and α-Si3N4 powder composition
    Liu, Yun
    Liu, Ruixiang
    Tong, Zongwei
    Zheng, Yuanhang
    Zhao, Jixue
    Sui, Tianyi
    Li, Xiaolei
    Lin, Bin
    JOURNAL OF ALLOYS AND COMPOUNDS, 2025, 1010
  • [49] Characterization of the Si3N4/Si3N4 joints fabricated using particles modified braze
    He, Yanming
    Zhang, Jie
    Li, Xiaodong
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 616 : 107 - 115
  • [50] High temperature microstructural stability of Si3N4 in TiAl alloys
    Choi, J. H.
    Lee, D. B.
    PROGRESS IN POWDER METALLURGY, PTS 1 AND 2, 2007, 534-536 : 1577 - +
12345