Formation of ceramic alumina nanocomposite coatings on aluminium for enhanced corrosion resistance

被引：105

作者：

Raj, V. ^{[1
]}

Ali, M. Mubarak ^{[1
]}

机构：

[1] Periyar Univ, Dept Chem, Adv Mat Res Lab, Salem 636011, India

来源：

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY | 2009年 / 209卷 / 12-13期

关键词：

Composite coating; Electrochemical impedance spectroscopy; Anodization; Aluminium; Corrosion protection; PLASMA ELECTROLYTIC OXIDATION; MICROARC OXIDATION; ANODIC FILMS; MECHANICAL-PROPERTIES; OXIDE COATINGS; ALLOY; GROWTH; PERFORMANCE; ADDITIVES; SILICATE;

D O I：

10.1016/j.jmatprotec.2009.04.004

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Plasma electrolytic oxidation (PEO) has been considered as a novel technique to form ceramic nanocomposite coatings on aluminium and magnesium alloys for corrosion protection. However, a systematic study of the effect of process parameters on the properties of the coatings has not been well demonstrated. In the present study, aluminium was treated by PEO at various treatment time. current density, temperature and concentration of NaOH and Na2SiO3 and their effect on the surface properties of the coatings has been investigated systematically. It was found that the temperature and treatment time were the major factors affecting the thickness and growth. The coatings mainly consisted of a-alumina, gamma-alumina and Al-2(SiO3)(3). The ceramic composite coatings with best corrosion resistance were obtained at higher current density, lower temperature, moderate treatment time and optimum concentration of NaOH and Na2SiO3. The crystallite size of the composite coating was found to be in nanometer scale (9-131 nm). (C) 2009 Elsevier B.V. All rights reserved.

引用

页码：5341 / 5352

页数：12

共 41 条

[11] Residual stresses in plasma electrolytic oxidation coatings on A1 alloy produced by pulsed unipolar current [J].

Khan, RHU ;

Yerokhin, AL ;

Pilkington, T ;

Leyland, A ;

Matthews, A .

SURFACE & COATINGS TECHNOLOGY, 2005, 200 (5-6) :1580-1586

[12] Structure and composition of anodic films formed on binary Mg-Al alloys in KOH-aluminate solutions under continuous sparking [J].

Khaselev, O ;

Weiss, D ;

Yahalom, J .

CORROSION SCIENCE, 2001, 43 (07) :1295-1307

[13] Characteristic of ceramic coatings on aluminum by plasma electrolytic oxidation in silicate and phosphate electrolyte [J].

Lv, Guohua ;

Gu, Weichao ;

Chen, Huan ;

Feng, Wenran ;

Khosa, M. Latif ;

Li, Li ;

Niu, Erwu ;

Zhang, Guling ;

Yang, Si-Ze .

APPLIED SURFACE SCIENCE, 2006, 253 (05) :2947-2952

[14] Systematic study of the electrolytic plasma oxidation process on a Mg alloy for corrosion protection [J].

Ma, Y ;

Nie, X ;

Northwood, DO ;

Hu, H .

THIN SOLID FILMS, 2006, 494 (1-2) :296-301

[15] Corrosion and erosion properties of silicate and phosphate coatings on magnesium [J].

Ma, Y ;

Nie, X ;

Northwood, DO ;

Hu, H .

THIN SOLID FILMS, 2004, 469 :472-477

[16]

MANFELD F, 1988, J ELECTROCHEM SOC, V135, P828

[17] ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY (EIS) AS A NEW TOOL FOR INVESTIGATING METHODS OF CORROSION PROTECTION [J].

MANSFELD, F .

ELECTROCHIMICA ACTA, 1990, 35 (10) :1533-1544

[18] A tracer study of oxide growth during spark anodizing of aluminum [J].

Monfort, F ;

Berkani, A ;

Matykina, E ;

Skeldon, P ;

Thompson, GE ;

Habazaki, H ;

Shimizu, K .

JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2005, 152 (06) :C382-C387

[19] Abrasive wear/corrosion properties and TEM analysis of Al2O3 coatings fabricated using plasma electrolysis [J].

Nie, X ;

Meletis, EI ;

Jiang, JC ;

Leyland, A ;

Yerokhin, AL ;

Matthews, A .

SURFACE & COATINGS TECHNOLOGY, 2002, 149 (2-3) :245-251

[20] Thickness effects on the mechanical properties of micro-arc discharge oxide coatings on aluminium alloys [J].

Nie, X ;

Leyland, A ;

Song, HW ;

Yerokhin, AL ;

Dowey, SJ ;

Matthews, A .

SURFACE & COATINGS TECHNOLOGY, 1999, 116 :1055-1060

← 1 2 3 4 5 →