High-temperature oxidation behavior of pure Ni3Al

被引：60
作者：
Choi, SC
Cho, HJ
Kim, YJ
Lee, DB
机构：
[1] Department of Metallurgical Engineering, Sung-Kyun-Kwan University
来源：
OXIDATION OF METALS | 1996年 / 46卷 / 1-2期
关键词：
Ni3Al; theta-Al2O3; alpha-Al2O3; oxidation mechanism;
D O I：
10.1007/BF01046884
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The high-temperature oxidation behaviour of pure Ni3Al alloys in air was studied above 1000 degrees C. In isothermal oxidation tests between 1000 and 1200 degrees C, Ni3Al showed parabolic oxidation behavior and displayed excellent oxidation resistance. In cyclic oxidation tests between 1000 and 1300 degrees C, Ni3Al exhibited excellent oxidation resistance between 1000 and 1200 degrees C, but drastic spalling of oxide scales was observed at 1300 degrees C. When Ni3Al was oxidized at 1000 degrees C, Al2O3 was present as theta-Al2O3 in a whisker form. But, at 1100 degrees C the gradual transformation of initially formed metastable theta Al2O3 to stable alpha-Al2O3 was observed after oxidation for about 20 hr. After oxidation at 1200 degrees C for long times, the formation of a thick columnar-grain layer of alpha-Al2O3 was observed beneath a thin and fine-grain outer layer of alpha-Al2O3. The oxidation mechanism of pure Ni3Al is described.
引用
收藏
页码：51 / 72
页数：22
相关论文
共 33 条
[11]   THE MICROSTRUCTURE OF THE SCALE FORMED DURING THE HIGH-TEMPERATURE OXIDATION OF A FECRALLOY STEEL [J].
MOSELEY, PT ;
HYDE, KR ;
BELLAMY, BA ;
TAPPIN, G .
CORROSION SCIENCE, 1984, 24 (06) :547-565
[12]   EFFECT OF YTTRIUM ADDITION ON THE HIGH-TEMPERATURE OXIDATION RESISTANCE OF NI3AL ALLOY [J].
OCHIAI, S ;
SUZUKI, T ;
KOJIMA, Y ;
KOBAYASHI, M ;
TORISAKA, Y .
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1989, 53 (06) :585-592
[13]   A THEORY OF THE ANOMALOUS YIELD BEHAVIOR IN LL2 ORDERED ALLOYS [J].
PAIDAR, V ;
POPE, DP ;
VITEK, V .
ACTA METALLURGICA, 1984, 32 (03) :435-448
[14]  
PETTIT FS, 1967, T METALL SOC AIME, V239, P1296
[15]   O-18/SIMS CHARACTERIZATION OF THE GROWTH-MECHANISM OF DOPED AND UNDOPED ALPHA-AL2O3 [J].
PINT, BA ;
MARTIN, JR ;
HOBBS, LW .
OXIDATION OF METALS, 1993, 39 (3-4) :167-195
[16]   THE OXIDATION MECHANISM OF THETA-AL2O3 SCALES [J].
PINT, BA ;
MARTIN, JR ;
HOBBS, LW .
SOLID STATE IONICS, 1995, 78 (1-2) :99-107
[17]  
PINT BA, 1992, THESIS MIT CAMBRIDGE
[18]  
PINT BA, 1994, J ELECTROCHEM SOC, V141, P2243
[19]   THE FORMATION OF ALUMINUM-OXIDE SCALES ON HIGH-TEMPERATURE ALLOYS [J].
PRESCOTT, R ;
GRAHAM, MJ .
OXIDATION OF METALS, 1992, 38 (3-4) :233-254
[20]  
PROVENZANO V, 1988, SURF COAT TECH, V36, P91
1234