Damage growth triggered by interface irregularities in thermal barrier coatings

被引：97
|
作者：
Hille, Thomas S. [2 ,3 ]
Nijdam, Thijs J. [1 ,2 ]
Suiker, Akke S. J. [3 ]
Turteltaub, Sergio [3 ]
Sloof, Wim G. [1 ]
机构：
[1] Delft Univ Technol, Dept Mat Sci & Engn, NL-2628 CD Delft, Netherlands
[2] Delft Univ Technol, M2i, NL-2629 HS Delft, Netherlands
[3] Delft Univ Technol, Fac Aerosp Engn, NL-2629 HS Delft, Netherlands
来源：
ACTA MATERIALIA | 2009年 / 57卷 / 09期
关键词：
Thermal barrier coating (TBC); Finite element modeling (FEM); Fracture; Diffusion; Oxidation; NICOCRALY BOND COATINGS; PREOXIDATION TREATMENT; MECHANICAL-PROPERTIES; FAILURE MECHANISMS; SYSTEMS; OXIDATION; DELAMINATION; DEPOSITION; ROUGHNESS; THICKNESS;
D O I：
10.1016/j.actamat.2009.01.022
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The efficiency and reliability of modern jet engines strongly depend on the performance of thermal barrier coatings (TBCs), which prevent melting and oxidation of the turbine blades' structural core. The system's lifetime is limited by cracks appearing in and in the vicinity of an oxide layer that grows in the TBC under thermal cycling. High replacement costs have led to an increased demand to identify, quantify and remedy damage in TBCs. An integrated experimental-numerical approach is presented for studying the main, particularly interfacial irregularities. Damage at several stages of oxidation in TBCs is analyzed in factors that contribute to damage. samples with predefined interfacial irregularities. The model predicts the experimentally observed crack patterns, clearly quantifying the influence of imperfections and indicating that damage can be delayed by Surface treatment. (C) 2009 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码：2624 / 2630
页数：7
相关论文
共 50 条
  • [1] Oxide growth and damage evolution in thermal barrier coatings
    Hille, T. S.
    Turteltaub, S.
    Suiker, A. S. J.
    ENGINEERING FRACTURE MECHANICS, 2011, 78 (10) : 2139 - 2152
  • [2] Damage Evolution in Thermal Barrier Coatings with Thermal Cycling
    Heeg, Bauke
    Tolpygo, Vladimir K.
    Clarke, David R.
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2011, 94 : S112 - S119
  • [3] Improved the Durability of Thermal Barrier Coatings with Interface Modified by Three-Dimensional Mesh Patterns
    Luo, L.
    Zhang, X.
    Zou, Z.
    Guo, F.
    Qi, H.
    Zhao, X.
    Xiao, P.
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2016, 99 (10) : 3406 - 3410
  • [4] Delamination crack growth in thermal barrier coatings
    Brodin, H
    Li, XH
    THERMAL SPRAY 2004: ADVANCES IN TECHNOLOGY AND APPLICATION, PROCEEDINGS, 2004, : 1088 - 1091
  • [5] Growth Behavior of Thermally Grown Oxide Layer with Bond Coat Species in Thermal Barrier Coatings
    Jung, Sung Hoon
    Jeon, Soo Hyeok
    Park, Hyeon-Myeong
    Jung, Yeon Gil
    Myoung, Sang Won
    Yang, Byung Il
    JOURNAL OF THE KOREAN CERAMIC SOCIETY, 2018, 55 (04) : 344 - 351
  • [6] Effect of Interface Curvature on Local Growth Behavior and Stress of Thermal Barrier Coatings
    Wang, Lulu
    Yu, Jun
    Zhang, Tao
    Wang, Zhe
    Ding, Kunying
    COATINGS, 2023, 13 (09)
  • [7] Buckling and interface strength analyses of thermal barrier coatings combining Laser Shock Adhesion Test to thermal cycling
    Guipont, Vincent
    Begue, Geoffrey
    Fabre, Gregory
    Maurel, Vincent
    SURFACE & COATINGS TECHNOLOGY, 2019, 378
  • [8] Temperature dependent dynamic growth of thermally grown oxide in thermal barrier coatings
    Lim, L. Y.
    Meguid, S. A.
    MATERIALS & DESIGN, 2019, 164
  • [9] Evaluation of interface reactions in thermal barrier ceramic coatings
    Celik, E
    Avci, E
    Yilmaz, F
    SURFACE & COATINGS TECHNOLOGY, 1997, 97 (1-3) : 361 - 365
  • [10] Crack-Growth Behavior in Thermal Barrier Coatings with Cyclic Thermal Exposure
    Song, Dowon
    Song, Taeseup
    Paik, Ungyu
    Lyu, Guanlin
    Jung, Yeon-Gil
    Choi, Baig-Gyu
    Kim, In-Soo
    Zhang, Jing
    COATINGS, 2019, 9 (06):
12345