An energetic approach to abrasive wear of a martensitic stainless steel

被引：9

作者：

Pamuk, U ^{[1
]}

Baydogan, M ^{[1
]}

Nilüfer, B ^{[1
]}

Çimenoglu, H ^{[1
]}

机构：

[1] Istanbul Tech Univ, Dept Met & Mat Sci Engn, TR-80626 Istanbul, Turkey

来源：

SCRIPTA MATERIALIA | 2000年 / 42卷 / 09期

关键词：

abrasion; aging; hardness; scratch;

D O I：

10.1016/S1359-6462(00)00307-9

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Hardness and scratch tests were performed to examine the abrasive wear behavior of martensitic stainless steel. Aging at 485°C for 1 h increased the abrasion resistance of 17-4 quality stainless steel about 50% with respect to as-received condition, by increasing specific energy of both penetration and grinding stages. However, the increment in the specific energy of penetration stage was much lower than that of grinding stage. In an abrasion process, grinding stage was more effective than penetration stage in determining the energy consumption rate and therefore the wear resistance of the investigated stainless steel.

引用

页码：881 / 885

页数：5

共 50 条

[21] Effect of applied magnetic field on wear behaviour of martensitic steel [J].

Fu, Licai ;

Zhou, Lingping .

JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2019, 8 (03) :2880-2886

[22] Effect of Pre-corrosion Damage on Dry Sliding Wear Behavior of Differently Heat-Treated Martensitic Stainless Steel [J].

Khare, Neelima ;

Bonagani, Sunil Kumar ;

Limaye, P. K. ;

Kumar, Naveen ;

Kain, Vivekanand .

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2024, 33 (02) :618-633

[23] Cavitation erosion resistance and wear mechanisms of active screen low temperature plasma nitrided AISI 410 martensitic stainless steel [J].

Espitia, L. A. ;

Dong, Hanshan ;

Li, Xiao-Ying ;

Pinedo, C. E. ;

Tschiptschin, A. P. .

WEAR, 2015, 332 :1070-1079

[24] Impact-abrasive wear of martensitic steels and complex iron-based hardfacing alloys [J].

Rojacz, H. ;

Katsich, C. ;

Kirchgassner, M. ;

Kirchmayer, R. ;

Badisch, E. .

WEAR, 2022, 492-493

[25] COMPARISON OF SLIDING WEAR AND THREE-BODY ABRASIVE WEAR CHARACTERISTICS OF PLAIN CARBON STEEL [J].

Kim, Yong-Suk ;

Yoon, Narae ;

Kim, Jong Chul .

INTERNATIONAL JOURNAL OF MODERN PHYSICS B, 2011, 25 (31) :4257-4260

[26] Studies on Wear Behaviour and DBTT in Sub-zero Regimes of Cryo-Treated High Nitrogen Martensitic Stainless Steel (HNMS) [J].

Shah, Naimish ;

Arora, Kapil ;

Dhokey, N. B. ;

Kumar, N. Dileep ;

Tharian, K. T. .

TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2019, 72 (08) :2121-2126

[27] Abrasive Wear Behaviour of Heat Treated En31 Steel [J].

Baburaj, Abin ;

Chaudhary, K. B. Shishupal Singh ;

Khatirkar, Rajesh K. ;

Sapate, Sanjay G. .

ISIJ INTERNATIONAL, 2013, 53 (08) :1471-1478

[28] Microstructure evolution and abrasive wear behavior of D2 steel [J].

Singh, Kritika ;

Khatirkar, Rajesh K. ;

Sapate, Sanjay G. .

WEAR, 2015, 328 :206-216

[29] THE INFLUENCE OF HEAT TREATNEMNT ON THE ABRASIVE WEAR RESISTNACE OF A CONSTRUCTION AND A TOOL STEEL [J].

Orecny, M. ;

Bursak, M. ;

Vinas, J. .

METALURGIJA, 2015, 54 (01) :191-193

[30] Particle erosion of SUS403 tempered martensitic stainless steel [J].

Wen, DC .

ISIJ INTERNATIONAL, 2006, 46 (05) :728-733

← 1 2 3 4 5 →