Influence of yttrium and vacuum degree on the purification of K417 superalloy

被引：17

作者：

Bian, Wei-dong ^{[1
]}

Zhang, Hua-rui ^{[1
]}

Gao, Ming ^{[1
]}

Li, Qing-ling ^{[1
]}

Li, Jin-peng ^{[1
]}

Tao, Tong-xiang ^{[2
]}

Zhang, Hu ^{[1
]}

机构：

[1] Beihang Univ, Sch Mat Sci & Engn, Beijing 100191, Peoples R China

[2] Beihang Univ, Qingdao Inst New Mat Technol, Qingdao 266000, Peoples R China

来源：

VACUUM | 2018年 / 152卷

基金：

中国国家自然科学基金;

关键词：

Yttrium; Vacuum degree; Deoxidation; Denitrogenation; Y2O3; crucibles; Superalloy; CASTING PROCESS; MICROSTRUCTURE; ALLOY;

D O I：

10.1016/j.vacuum.2018.02.031

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

K417 superalloy castings with different addition of rare earth element Y were produced by vacuum induction melting technology using Y2O3 crucibles under different vacuum degrees. The effects and interaction mechanisms of Y and vacuum degree on the purification of the superalloy were investigated. The results showed that high purification of K417 superalloy with 4 similar to 5 ppm O and N was obtained after addition of Y. There was a characteristic transition during the deoxidation and denitrogenation of the superalloy when the vacuum degree changed. With the addition of 0.5 wt% Y in the alloy, the concentration of O could be reduced from 34 ppm to 8 ppm in rough vacuum and from 13 ppm to 4 ppm in high vacuum, respectively. High vacuum enhanced the chemical dissolution of Y2O3 crucible. The concentration of N decreased from 43 ppm to 14 ppm with the addition of Y in rough vacuum condition of 100Pa. Whereas, in high vacuum condition of 0.035Pa, the concentration of N tend to increase from 4 ppm to 7 ppm. The effect of deoxidation of Y promoted the process of denitrogenation. (C) 2018 Elsevier Ltd. All rights reserved.

引用

页码：57 / 64

页数：8

共 22 条

[1]

Bai H. B., 2015, MATER RES INNOV, V18

[2] Investigation on strain dependence of metadynamic recrystallization behaviors of GH4169 superalloy [J].

Chen, Xiao-Min ;

Lin, Y. C. ;

Li, Xin-He ;

Chen, Ming-Song ;

Yuan, Wu-Quan .

VACUUM, 2018, 149 :1-11

[3] Interactions between TiAl alloys and yttria refractory material in casting process [J].

Cui Renjie ;

Gao Ming ;

Zhang Hu ;

Gong Shengkai .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2010, 210 (09) :1190-1196

[4]

Dong J.S., 2008, MAT REPORTS, V22, P445

[5] Effects of grain refinement on the microstructure and tensile behavior of K417G superalloy [J].

Du, Beining ;

Yang, Jinxia ;

Cui, Chuanyong ;

Sun, Xiaofeng .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 623 :59-67

[6] Physical erosion of yttria crucibles in Ti-54Al alloy casting process [J].

Gao Ming ;

Cui Renjie ;

Ma Limin ;

Zhang Huarui ;

Tang Xiaoxia ;

Zhang Hu .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2011, 211 (12) :2004-2011

[7]

Geng X., 2015, J MAT METALL, V14, P175

[8] Effect of N content on microsegregation, microstructure and mechanical property of cast Ni-base superalloy K417G [J].

Gong, Li ;

Chen, Bo ;

Yang, Yaqian ;

Du, Zhanhui ;

Liu, Kui .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2017, 701 :111-119

[9]

[金玉花 Jin Yuhua], 2016, [材料工程, Journal of Materials Engineering], V44, P46

[10] Effects of rare earth yttrium on microstructure and properties of Ni-16Mo-7Cr-4Fe nickel-based superalloy [J].

Li, X. L. ;

He, S. M. ;

Zhou, X. T. ;

Zou, Y. ;

Li, Z. J. ;

Li, A. G. ;

Yu, X. H. .

MATERIALS CHARACTERIZATION, 2014, 95 :171-179

← 1 2 3 →