Preparation of nano α-alumina powder and wear resistance of nanoparticles reinforced composite coating

被引:25
作者
Chen, Caifeng [1 ]
Ding, Zhidan [1 ]
Tan, Qi [1 ]
Qi, Henghua [1 ]
He, Yonghui [1 ]
机构
[1] Jiangsu Univ, Sch Mat Sci & Engn, Zhenjiang 212013, Jiangsu, Peoples R China
基金
中国国家自然科学基金;
关键词
Preparation; Nano; alpha-Alumina; Thermal spraying; Coating; THERMAL BARRIER; BOEHMITE;
D O I
10.1016/j.powtec.2014.02.059
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
Nanometer alpha-alumina powder was synthesized using the pore rich activated carbon as the reaction place, and the alpha-alumina nanopartide reinforced nickel based composite coating was prepared by flash thermal spray method. The composite coating was abraded on abrasive wear-machine to study its wear resistance property. The results showed that a large number of uniform size spherical-shaped precursor particles were in the activated carbon pores, which could be long-term stable in a spherical shape and adsorbed on the pore wall. In addition, activated carbon pores could prevent the alumina particles from growing up and reuniting effectively during the precursor particles calcination process. And the activated carbon had completely burned at high temperature as well. Finally, nano alpha-alumina powder with good dispersion was obtained. The wear resistance of the nickel based composite coating was reinforced by the nanometer alpha-alumina powder. With 2% volume fraction addition of nanometer alpha-alumina, the coating has the best abrasive wear resistance property. (C) 2014 Elsevier B.V. All rights reserved.
引用
收藏
页码:83 / 87
页数:5
相关论文
共 14 条
[1]   Specific signatures of α-alumina powders prepared by calcination of boehmite or gibbsite [J].
Boumaza, A. ;
Djelloul, A. ;
Guerrab, F. .
POWDER TECHNOLOGY, 2010, 201 (02) :177-180
[2]   Formation of a dense and continuous Al2O3 layer in nano thermal barrier coating systems for the suppression of spinel growth on the Al2O3 oxide scale during oxidation [J].
Daroonparvar, Mohammadreza ;
Yajid, Muhamad Azizi Mat ;
Yusof, Noordin Mohd ;
Hussain, Mohammad Sakhawat ;
Bakhsheshi-Rad, Hamid Reza .
JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 571 :205-220
[3]   Sintering of monodoped and mixtures of monodoped alpha alumina powders [J].
Hilli, N. ;
Goeuriot, P. .
POWDER TECHNOLOGY, 2009, 190 (1-2) :129-133
[4]  
Isfahani T.D., 2012, J POWDER TECHNOL, V299, P17
[5]   Preparation and sintering pure nanocrystalline α-alumina powder [J].
Karagedov, G. R. ;
Myz, A. L. .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2012, 32 (01) :219-225
[6]   Synthesis of alumina nanoparticle-embedded-bismuth telluride matrix thermoelectric composite powders [J].
Kim, Kyung Tae ;
Koo, Hye Young ;
Lee, Gil-Geun ;
Ha, Gook Hyun .
MATERIALS LETTERS, 2012, 82 :141-144
[7]   Thermal spray coatings engineered from nanostructured ceramic agglomerated powders for structural, thermal barrier and biomedical applications: A review [J].
Lima, R. S. ;
Marple, B. R. .
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2007, 16 (01) :40-63
[8]   Effect of particle size distribution on sintering of agglomerate-free submicron alumina powder compacts [J].
Ma, J ;
Lim, LC .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2002, 22 (13) :2197-2208
[9]   Synthesis, properties and optimization of the rheological behaviors on alumina and zinc aluminate powders obtained from dicarboxylate precursors [J].
Nikumbh, Arvind K. ;
Adhyapak, Parag V. .
POWDER TECHNOLOGY, 2010, 202 (1-3) :14-23
[10]   Production of micro-crystalline boehmite from hydrothermal processing of Bayer plant alumina tri-hydrate [J].
Oh, Chi Jung ;
Yi, Youn Kyu ;
Kim, Seong Jun ;
Tam Tran ;
Kim, Myong Jun .
POWDER TECHNOLOGY, 2013, 235 :556-562