Determination of critical condition for initiation of dynamic recrystallisation in Zr-1%Nb alloy

被引:10
作者
Saboori, Abdollah [1 ]
Pavese, Matteo [1 ]
Biamino, Sara [1 ]
Fino, Paolo [1 ]
Lombardi, Mariangela [1 ]
机构
[1] Politecn Torino, Dept Appl Sci & Technol, Corso Duca Abruzzi 24, Turin, Italy
关键词
Hot deformation; Critical stress; Work hardening rate; Dynamic recrystallisation (DRX); Microstructure; Zr alloy; HOT DEFORMATION-BEHAVIOR; HIGH-TEMPERATURE; CRITICAL STRAIN; FLOW-STRESS; ZR-2.5NB; STEEL; CURVE;
D O I
10.1016/j.jallcom.2018.05.052
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The critical stress and strain for initiation of dynamic recrystallisation (DRX) in Zr-1%Nb alloy have been determined by employing two different approaches. The work hardening rate versus stress curve and the natural logarithm of work hardening rate versus strain were used for this analysis. To evaluate the onset of DRX in Zr-1%Nb alloy, the hot deformation behaviour of this alloy has been studied in the temperature range of 770-850 degrees C and strain rates range 10(-2) to 1 s(-1). To reduce friction during the tests, the ends of samples were coated with graphite powder and a thin layer of mica placed between the surface of samples and the anvils. Nevertheless, the flow stress values were corrected to eliminate the effects of friction and adiabatic heating during the tests. The outcomes of work hardening rate analysis showed that the first method (work hardening rate versus stress) is the best method to determine the critical conditions of initiation of DRX. All in all, for Zr-1%Nb alloy, the dynamic recrystallisation was found to start when the normalised stress and strain reach the values of 0.91 and 0.87, respectively. Furthermore, the transmission electron microscopy (TEM) analysis showed that the DRX took place through a continuous mechanism, and optical microstructures confirmed that at low temperature and high strain rate the flow curves could be explained by localised deformation and shear band formation. (C) 2018 Elsevier B.V. All rights reserved.
引用
收藏
页码:1 / 7
页数:7
相关论文
共 32 条
[1]  
[Anonymous], 1988, THERMOMECHANICAL PRO
[2]   Predicting the critical strain for dynamic recrystallization using the kinetics of static recrystallization [J].
Barnett, MR ;
Kelly, GL ;
Hodgson, PD .
SCRIPTA MATERIALIA, 2000, 43 (04) :365-369
[3]   Effect of predeformation on microstructural evolution of a Zr alloy during 550-700 °C aging after β quenching [J].
Chai, Linjiang ;
Luan, Baifeng ;
Murty, Korukonda L. ;
Liu, Qing .
ACTA MATERIALIA, 2013, 61 (08) :3099-3109
[4]   Characterization of hot deformation behavior of Zr-1Nb-1Sn alloy [J].
Chakravartty, J. K. ;
Kapoor, R. ;
Banerjee, S. ;
Prasad, Y. V. R. K. .
JOURNAL OF NUCLEAR MATERIALS, 2007, 362 (01) :75-86
[5]   Hot deformation and recrystallization of austenitic stainless steel: Part I. Dynamic recrystallization [J].
Dehghan-Manshadi, A. ;
Barnett, Mr. ;
Hodgson, P. D. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2008, 39A (06) :1359-1370
[6]  
Dieter GE., 1976, MECH METALLURGY
[7]   Flow stress modeling and warm rolling simulation behavior of two Ti-Nb interstitial-free steels in the ferrite region [J].
Huang, C ;
Hawbolt, EB ;
Chen, X ;
Meadowcroft, TR ;
Matlock, DK .
ACTA MATERIALIA, 2001, 49 (08) :1445-1452
[8]   The Avrami kinetics of dynamic recrystallization [J].
Jonas, John J. ;
Quelennec, Xavier ;
Jiang, Lan ;
Martin, Etienne .
ACTA MATERIALIA, 2009, 57 (09) :2748-2756
[9]   Characterization of hot deformation behaviour of Zr-2.5Nb in β phase [J].
Kapoor, R ;
Chakravartty, JK .
JOURNAL OF NUCLEAR MATERIALS, 2002, 306 (2-3) :126-133
[10]   Correcting the Stress-Strain Curve in Hot Compression Process to High Strain Level [J].
Li, Y. P. ;
Onodera, E. ;
Matsumoto, H. ;
Chiba, A. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (04) :982-990