An easy co-casting method to synthesize mesostructured carbon composites with high magnetic separability and acid resistance

被引:16
作者
Guo, Limin [1 ]
Zeng, Shaozhong [1 ]
Li, Jiangtian [1 ]
Cui, Fangming [1 ]
Cui, Xiangzhi [1 ]
Bu, Wenbo [1 ]
Shi, Jianlin [1 ]
机构
[1] Chinese Acad Sci, Shanghai Inst Ceram, State Key Lab High Performance Ceram & Superfine, Shanghai 200050, Peoples R China
基金
美国国家科学基金会;
关键词
ORDERED MESOPOROUS CARBONS; MOLECULAR-SIEVES; FACILE SYNTHESIS; SURFACE FUNCTIONALIZATION; CRYSTALLINE WALLS; SILICA MATERIALS; HOLLOW SPHERES; CATALYST; TEMPLATE; NANOPARTICLES;
D O I
10.1039/b906776k
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
Magnetic mesoporous carbon composites with high surface areas and narrow mesopore size distributions were directly replicated from SBA-15 by a simple co-casting method and the amount of incorporated magnetic particles and saturation magnetization value can be easily tuned by changing the added amount of iron source during synthesis. Furthermore, the magnetic mesoporous carbon composites show good acid resistance due to a carbon shell coating structure around the magnetic particles, which is spontaneously formed during the replication process of the mesoporous carbon composites. The characteristics of the as-synthesized magnetic mesoporous carbon composites were examined by X-ray diffraction, N-2 sorption, transmission electron microscopy (TEM), Mossbauer spectroscopy and vibrating-sample magnetometry.
引用
收藏
页码:1926 / 1931
页数:6
相关论文
共 65 条
  • [21] ORDERED MESOPOROUS MOLECULAR-SIEVES SYNTHESIZED BY A LIQUID-CRYSTAL TEMPLATE MECHANISM
    KRESGE, CT
    LEONOWICZ, ME
    ROTH, WJ
    VARTULI, JC
    BECK, JS
    [J]. NATURE, 1992, 359 (6397) : 710 - 712
  • [22] Characterization of MCM-48 silicas with tailored pore sizes synthesized via a highly efficient procedure
    Kruk, M
    Jaroniec, M
    Ryoo, R
    Joo, SH
    [J]. CHEMISTRY OF MATERIALS, 2000, 12 (05) : 1414 - 1421
  • [23] Simple synthesis of mesoporous carbon with magnetic nanoparticles embedded in carbon rods
    Lee, J
    Jin, SM
    Hwang, Y
    Park, JG
    Park, HM
    Hyeon, T
    [J]. CARBON, 2005, 43 (12) : 2536 - 2543
  • [24] Adsorption and degradation of the cationic dyes over Co doped amorphous mesoporous titania-silica catalyst under UV and visible light irradiation
    Li, Junjie
    Liu, Shiqing
    He, Yuyang
    Wang, Jiaqiang
    [J]. MICROPOROUS AND MESOPOROUS MATERIALS, 2008, 115 (03) : 416 - 425
  • [25] A novel and simple in-situ reduction route for the synthesis of an ultra-thin metal nanocoating in the channels of mesoporous silica materials
    Li, L
    Shi, JL
    Zhang, LX
    Xiong, LM
    Yan, JN
    [J]. ADVANCED MATERIALS, 2004, 16 (13) : 1079 - +
  • [26] Synthesis of rhodium colloidal nano-coating grafted mesoporous silica composite and its application as efficient environmentally benign catalyst for heck-type reaction of arylboronic acids
    Li, Liang
    Shi, Jianlin
    [J]. ADVANCED SYNTHESIS & CATALYSIS, 2008, 350 (05) : 667 - 672
  • [27] In situ assembly of layered double hydroxide nano-crystallites within silica mesopores and its high solid base catalytic activity
    Li, Liang
    Shi, Jianlin
    [J]. CHEMICAL COMMUNICATIONS, 2008, (08) : 996 - 998
  • [28] Hollow spheres of mesoporous aluminosilicate with a three-dimensional pore network and extraordinarily high hydrothermal stability
    Li, YS
    Shi, JL
    Hua, ZL
    Chen, HR
    Ruan, ML
    Yan, DS
    [J]. NANO LETTERS, 2003, 3 (05) : 609 - 612
  • [29] Surface functionalization of ordered mesoporous carbons - A comparative study
    Li, ZJ
    Yan, WF
    Dai, S
    [J]. LANGMUIR, 2005, 21 (25) : 11999 - 12006
  • [30] Surface functionalization and pore size manipulation for carbons of ordered structure
    Li, ZJ
    Dai, S
    [J]. CHEMISTRY OF MATERIALS, 2005, 17 (07) : 1717 - 1721