Very-high-cycle fatigue crack initiation and propagation behaviours of magnesium alloy ZK60

被引：18
|
作者：
He, Chao [1 ,3 ]
Liu, Yongjie [2 ]
Li, Jiukai [2 ]
Yang, Kun [2 ]
Wang, Qingyuan [1 ,2 ]
Chen, Qiang [3 ]
机构：
[1] Chengdu Univ, Sch Architecture & Civil Engn, Chengdu, Sichuan, Peoples R China
[2] Sichuan Univ, Key Lab Deep Earth Sci & Engn, Minist Educ, Chengdu 610065, Sichuan, Peoples R China
[3] Kyushu Univ, Micromech Lab, Fac Engn, Fukuoka, Japan
来源：
MATERIALS SCIENCE AND TECHNOLOGY | 2018年 / 34卷 / 06期
关键词：
Fatigue crack initiation; fatigue crack propagation rate; magnesium alloy; very-high-cycle fatigue; HIGH-STRENGTH STEELS; DUPLEX STAINLESS-STEEL; VHCF REGIME; TITANIUM-ALLOY; GIGACYCLE FATIGUE; INCLUSIONS; DAMAGE; MECHANISMS; FRACTURE; SLIP;
D O I：
10.1080/02670836.2017.1407556
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The aim of this paper is to assess the very-high-cycle fatigue (VHCF) behaviour of a magnesium alloy (ZK60). Results indicate that the fatigue crack initiates from an area consisting of many distributed facets, while the region of early crack propagation is characterised by parallel traces, based on a fractographic analysis. The significant differences in morphology around the crack initiation area result from the interaction between the deformation twinning and the plastic zone at the crack tip. In addition, the fatigue crack propagation rate around the crack initiation site is also estimated based on a modified Murakami model. It is found that the formation stage for the fatigue crack is of great importance to the fatigue failure mechanism in the VHCF regime.
引用
收藏
页码：639 / 647
页数：9
相关论文
共 50 条
  • [21] Ratcheting deformation and fatigue of surface treated ZK60 magnesium alloy
    Xiong, Ying
    Yu, Yi
    INTERNATIONAL JOURNAL OF FATIGUE, 2022, 156
  • [22] Microstructure features induced by fatigue crack initiation up to very-high-cycle regime for an additively manufactured aluminium alloy
    Pan, Xiangnan
    Du, Leiming
    Qian, Guian
    Hong, Youshi
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2024, 173 : 247 - 260
  • [23] Internal crack characteristics in very-high-cycle fatigue of a gradient structured titanium alloy
    Pan, Xiangnan
    Qian, Guian
    Wu, Shengchuan
    Fu, Yanan
    Hong, Youshi
    SCIENTIFIC REPORTS, 2020, 10 (01)
  • [24] Internal crack characteristics in very-high-cycle fatigue of a gradient structured titanium alloy
    Xiangnan Pan
    Guian Qian
    Shengchuan Wu
    Yanan Fu
    Youshi Hong
    Scientific Reports, 10
  • [25] Microstructural Influences on Very-High-Cycle Fatigue-Crack Initiation in Ti-6246
    Szczepanski, C. J.
    Jha, S. K.
    Larsen, J. M.
    Jones, J. W.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2008, 39A (12): : 2841 - 2851
  • [26] Microstructural Influences on Very-High-Cycle Fatigue-Crack Initiation in Ti-6246
    C.J. Szczepanski
    S.K. Jha
    J.M. Larsen
    J.W. Jones
    Metallurgical and Materials Transactions A, 2008, 39 : 2841 - 2851
  • [27] Effect of pH on the corrosion and crack growth behavior of the ZK60 magnesium alloy
    Sun, Kaiqiang
    Gao, Hong
    Hu, Jiaqi
    Yan, Yingzhu
    CORROSION SCIENCE, 2021, 179
  • [28] Hot workability of magnesium alloy ZK60
    Mwembela, A
    McQueen, HJ
    HOT WORKABILITY OF STEELS & LIGHT ALLOYS-COMPOSITES, 1996, : 181 - 188
  • [29] Propensities of crack interior initiation and early growth for very-high-cycle fatigue of high strength steels
    Hong, Youshi
    Lei, Zhengqiang
    Sun, Chengqi
    Zhao, Aiguo
    INTERNATIONAL JOURNAL OF FATIGUE, 2014, 58 : 144 - 151
  • [30] Effect of microstructure inhomogeneity and crack initiation environment on the very high cycle fatigue behavior of a magnesium alloy
    Chen, Yao
    He, Chao
    Liu, Fulin
    Wang, Chong
    Xie, Qing
    Wang, Qingyuan
    Liu, Yongjie
    INTERNATIONAL JOURNAL OF FATIGUE, 2020, 131
12345