The adhesion of alumina films to metallic alloys and coatings

被引:0
作者
Sarioglu, C
Stiger, MJ
Blachere, JR
Janakiraman, R
Schumann, E
Ashary, A
Pettit, FS
Meier, GH
机构
[1] Univ Pittsburgh, Dept Mat Sci & Engn, Pittsburgh, PA 15261 USA
[2] Marmara Univ, Dept Mat Engn, Istanbul, Turkey
[3] Donsco Corp, Wrightsville, PA USA
[4] Siemens AG, Mulheim, Germany
[5] Praxair, Miami, FL USA
来源
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION | 2000年 / 51卷 / 05期
关键词
D O I
暂无
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The adherence of protective oxide scales to alloy substrates is governed by the stored elastic energy in the scale which drives delamination and the fracture resistance of the alloy oxide interface. Clearly any modifications to the alloy or the exposure environment which decreases the former or increases the latter will improve the durability of a given system. The stored elastic energy is determined by the stress level in the scale and the scale thickness. The stress state in the scale is determined by stresses which arise during the oxide formation (Growth Stresses). stresses produced during temperature changes as the re suit of thermal expansion mismatch between the oxide and the alloy (Thermal Stresses), and any stress relaxation which occurs as the result of creep of the scale or alloy. The fracture energy of the interface is a function of the composition at the interface, the microstructure in the interfacial region, and the composition of the exposure environment. This paper focuses on the results of studies of a variety of alloys and coatings. all of which form continuous alumina scales, in which it has been attempted to evaluate the effects of various alloy and exposure parameters on the stress state in the scale, the microstructure of the alloy/oxide interface, and the fracture resistance of the interface. The alloy parameters include alloy type, sulfur content, and reactive element content. The exposure parameters include oxidation temperature, temperature profile during exposure, and water vapor and sulfur contents of the atmosphere.
引用
收藏
页码:358 / 372
页数:15
相关论文
共 73 条
[11]   Measurement of the adhesion of a brittle film on a ductile substrate by indentation [J].
Drory, MD ;
Hutchinson, JW .
PROCEEDINGS OF THE ROYAL SOCIETY A-MATHEMATICAL PHYSICAL AND ENGINEERING SCIENCES, 1996, 452 (1953) :2319-2341
[12]   Effect of interface undulations on the thermal fatigue of thin films and scales on metal substrates [J].
Evans, AG ;
He, MY ;
Hutchinson, JW .
ACTA MATERIALIA, 1997, 45 (09) :3543-3554
[13]   CONDITIONS FOR THE INITIATION OF OXIDE SCALE CRACKING AND SPALLATION [J].
EVANS, HE ;
LOBB, RC .
CORROSION SCIENCE, 1984, 24 (03) :209-222
[14]  
EVANS UR, 1948, INTRO METALLIC CORRO, P194
[16]   The theory of metal-ceramic interfaces [J].
Finnis, MW .
JOURNAL OF PHYSICS-CONDENSED MATTER, 1996, 8 (32) :5811-5836
[17]   CREEP OF DUPLEX MICROSTRUCTURES [J].
FRENCH, JD ;
ZHAO, JH ;
HARMER, MP ;
CHAN, HM ;
MILLER, GA .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1994, 77 (11) :2857-2865
[18]   REACTIVE ELEMENT - SULFUR INTERACTION AND OXIDE SCALE ADHERENCE [J].
FUNKENBUSCH, AW ;
SMEGGIL, JG ;
BORNSTEIN, NS .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (06) :1164-1166
[19]   The influence of chromium addition on the toughness of gamma-Ni/alpha-Al2O3 interfaces [J].
Gaudette, F ;
Suresh, S ;
Evans, AG ;
Dehm, G ;
Ruhle, M .
ACTA MATERIALIA, 1997, 45 (09) :3503-3513
[20]   OXIDATION OF NI-CR-AL ALLOYS BETWEEN 1000 DEGREES AND 1200 DEGREES C [J].
GIGGINS, CS ;
PETTIT, FS .
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1971, 118 (11) :1782-&