Fabrication, mechanical properties, and tribological behaviors of Ti2AlC and Ti2AlSn0.2C solid solutions

被引:47
作者
Cai, Leping [1 ]
Huang, Zhenying [1 ,2 ]
Hu, Wenqiang [1 ]
Hao, Suming [1 ]
Zhai, Hongxiang [1 ]
Zhou, Yang [1 ]
机构
[1] Beijing Jiaotong Univ, Ctr Mat Sci & Engn, Sch Mech & Elect Control Engn, Beijing 100044, Peoples R China
[2] Beijing Jiaotong Univ, Minist Educ, Key Lab Vehicle Adv Mfg Measuring & Control Techn, Beijing, Peoples R China
基金
中国国家自然科学基金;
关键词
Ti2AlC; Ti2AlSn0.2C; microstructure; mechanical property; tribological behavior; GRAIN-SIZE; TI3ALC2; MICROSTRUCTURE; OXIDATION; COMPOSITES; FRICTION; SURFACE; PHASES;
D O I
10.1007/s40145-017-0221-9
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Highly pure and dense Ti2AlC and Ti2AlSn0.2C bulks were prepared by hot pressing with molar ratios of 1:1.1:0.9 and 1:0.9:0.2:0.85, respectively, at 1450 degrees C for 30 min with 28 MPa in Ar atmosphere. The phase compositions were investigated by X-ray diffraction (XRD); the surface morphology and topography of the crystal grains were also analyzed by scanning electron microscopy (SEM). The flexural strengths of Ti2AlC and Ti2AlSn0.2C have been measured as 430 and 410 MPa, respectively. Both Vickers hardness decreased slowly as the load increased. The tribological behavior was investigated by dry sliding a low-carbon steel under normal load of 20-80 N and sliding speed of 10-30 m/s. Ti2AlC bulk has a friction coefficient of 0.3-0.45 and a wear rate of (1.64-2.97)x10(-6) mm(3)/(N.m), while Ti2AlSn0.2C bulk has a friction coefficient of 0.25-0.35 and a wear rate of (2.5-4.31) x10(-6) mm(3)/(N.m). The influences of Sn incorporation on the microstructure and properties of Ti2AlC have also been discussed.
引用
收藏
页码:90 / 99
页数:10
相关论文
共 31 条
  • [1] Processing and characterization of Ti2AlC, Ti2AlN, and Ti2AlC0.5N0.5
    Barsoum, MW
    Ali, M
    El-Raghy, T
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2000, 31 (07): : 1857 - 1865
  • [2] The MN+1AXN phases:: A new class of solids;: Thermodynamically stable nanolaminates
    Barsoum, MW
    [J]. PROGRESS IN SOLID STATE CHEMISTRY, 2000, 28 (1-4) : 201 - 281
  • [3] Oxidation of Tin+1AlXn (n=1-3 and X = C, N) -: II.: Experimental results
    Barsoum, MW
    Tzenov, N
    Procopio, A
    El-Raghy, T
    Ali, M
    [J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2001, 148 (08) : C551 - C562
  • [4] Synthesis, Characterization, and Intrinsic Hardness of Layered Nanolaminate Ti3AlC2 and Ti3Al0.8Sn0.2C2 Solid Solution
    Bei, G. P.
    Gauthier-Brunet, V.
    Tromas, C.
    Dubois, S.
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2012, 95 (01) : 102 - 107
  • [5] Crack Healing in Ti2Al0.5Sn0.5C-Al2O3 Composites
    Bei, Guo Ping
    Pedimonte, Birgit Joana
    Pezoldt, Marc
    Ast, Johannes
    Fey, Tobias
    Goeken, Mathias
    Greil, Peter
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2015, 98 (05) : 1604 - 1610
  • [6] Oxidation Behavior of MAX Phase Ti2Al(1-x)SnxC Solid Solution
    Bei, Guoping
    Pedimonte, Birgit-Joana
    Fey, Tobias
    Greil, Peter
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2013, 96 (05) : 1359 - 1362
  • [7] Abnormal thermal expansion and thermal stability of Ti3Al1-xSixC2 solid solutions
    Chen, J. X.
    Zhou, Y. C.
    Zhang, J.
    [J]. SCRIPTA MATERIALIA, 2006, 55 (08) : 675 - 678
  • [8] Synthesis, Microstructure, and Mechanical Properties of Ti3Sn(1-x)AlxC2 MAX Phase Solid Solutions
    Dubois, Sylvain
    Bei, Guo P.
    Tromas, Christophe
    Gauthier-Brunet, Veronique
    Gadaud, Pascal
    [J]. INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2010, 7 (06) : 719 - 729
  • [9] Processing and mechanical properties of Ti3SiC2:: II, effect of grain size and deformation temperature
    El-Raghy, T
    Barsoum, MW
    Zavaliangos, A
    Kalidindi, SR
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1999, 82 (10) : 2855 - 2860
  • [10] Effect of grain size on friction and wear behavior of Ti3SiC2
    El-Raghy, T
    Blau, P
    Barsoum, MW
    [J]. WEAR, 2000, 238 (02) : 125 - 130