Synthesis of protective Mo-Si-B coatings in molten salts and their oxidation behavior in an air-water mixture

被引：37
作者：
Kuznetsov, Sergey A.
Rebrov, Evgeny V.
Mies, Martijn J. M.
de Croon, Mart H. J. M.
Schouten, Jaap C.
机构：
[1] Eindhoven Univ Technol, Lab Chem Reactor Engn, NL-5600 MB Eindhoven, Netherlands
[2] Russian Acad Sci, Kola Sci Ctr, Inst Chem, Apatity 184209, Murmansk Reg, Russia
来源：
SURFACE & COATINGS TECHNOLOGY | 2006年 / 201卷 / 3-4期
关键词：
electrochemical deposition; MoSi2; molten salts; molybdenum; boronizing; oxidation resistance;
D O I：
10.1016/j.surfcoat.2006.01.003
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The formation of various phases during boronizing of silicided molybdenum substrates (MoSi2/Mo) was investigated. Boronizing treatments were conducted in molten salts under an inert gas atmosphere in the 700-1000 degrees C temperature range for 3-7 h. Depending on the process type (non-current or electrochemical) and molten salt temperature, the formation of different boride phases (MoB, Mo2B5, MoB2, MoB4) was observed. At the same time, substantial oxidation of the bulk molybdenum disilicide phase (MoSi2) to the Mo5Si3 phase was observed in non-current boronizing. The oxidation resistance of the coatings was investigated by the weight change in an air-water (2.3 vol.%) mixture at a temperature of 500 degrees C for a period up to 700 h. Results indicated that a two-phase microstructure consisting of the MoSi2, matrix phase with 12-15 wt.% of the MoB4 phase greatly improved the oxidation resistance of the molybdenum substrates. The weight gain rate observed was 6.5 center dot 10(-4) mg/cm(2) h. (c) 2006 Elsevier B.V. All rights reserved.
引用
收藏
页码：971 / 978
页数：8
相关论文
共 36 条
[1]   Boron-doped molybdenum silicides for structural applications [J].
Akinc, M ;
Meyer, MK ;
Kramer, MJ ;
Thom, AJ ;
Huebsch, JJ ;
Cook, B .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 261 (1-2) :16-23
[2]  
Berczik D.M., 1997, US Patent, Patent No. 5595616
[3]   STRUCTURAL AND MORPHOLOGICAL-STUDIES OF THE GROWTH OF MOO3 SCALES DURING HIGH-TEMPERATURE OXIDATION OF MOLYBDENUM [J].
FLOQUET, N ;
BERTRAND, O ;
HEIZMANN, JJ .
OXIDATION OF METALS, 1992, 37 (3-4) :253-280
[4]   Phase stability, bonding mechanism, and elastic constants of Mo5Si3 by first-principles calculation [J].
Fu, CL ;
Wang, XD ;
Ye, YY ;
Ho, KM .
INTERMETALLICS, 1999, 7 (02) :179-184
[5]   Solubility of boron in Mo5+ySi3-y [J].
Huebsch, JJ ;
Kramer, MJ ;
Zhao, HL ;
Akinc, M .
INTERMETALLICS, 2000, 8 (02) :143-150
[6]  
Jones E. S., 1958, CORROSION, V14, P20, DOI 10.5006/0010-9312-14.1.20
[7]  
Kaptay G., 1999, Plasmas Ions, V2, P45, DOI DOI 10.1016/S1288-3255(00)87686-8
[8]   Low temperature oxidation of fully dense and porous MoSi2 [J].
Kurokawa, K ;
Houzumi, H ;
Saeki, I ;
Takahashi, H .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 261 (1-2) :292-299
[9]   Synthesis of molybdenum borides and molybdenum silicides in molten salts and their oxidation behavior in an air-water mixture [J].
Kuznetsov, SA ;
Kuznetsova, SV ;
Rebrov, E ;
Mies, MJM ;
de Croon, K ;
Schouten, JC .
SURFACE & COATINGS TECHNOLOGY, 2005, 195 (2-3) :182-188
[10]  
KUZNETSOV SA, 1999, RUSS J ELECTROCHEM+, V35, P1301
1234