Metastable pitting corrosion of 304 stainless steel in 3.5% NaCl solution

被引：230

作者：

Tian, Wenming ^{[1
]}

Du, Nan ^{[2
]}

Li, Songmei ^{[1
]}

Chen, Sibing ^{[2
]}

Wu, Qunying ^{[2
]}

机构：

[1] Beihang Univ, Sch Mat Sci & Engn, Beijing 100191, Peoples R China

[2] Nanchang Hangkong Univ, Inst Sci & Technol, Natl Def Key Discipline Lab Light Alloy Proc, Nanchang 330063, Peoples R China

来源：

CORROSION SCIENCE | 2014年 / 85卷

关键词：

Stainless steel; Polarization; Pitting corrosion; Kinetic parameters; STAINLESS-STEEL; CHLORIDE SOLUTION; SURFACE-ROUGHNESS; MILD-STEEL; NUCLEATION; PITS; GROWTH; BICARBONATE; BEHAVIORS; STABILITY;

D O I：

10.1016/j.corsci.2014.04.033

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Metastable pitting corrosion of 304 stainless steel was studied by potentiostatic polarization and three-dimensional video microscope. The results showed that the dissolution rate of metastable pits increased with time, and peaked before repassivation. The average lifetime of metastable pits decayed with potential. Whereas maximum pit lifetime, average peak value of current transients and pitting nucleation numbers increased with potential. Metastable pits were transformed from cone-shaped to dish-shaped during metastable growth. The ohmic potential drop presented between the pit interior and bulk solution, but the growth controlling factor was metal cations diffusion. (C) 2014 Elsevier Ltd. All rights reserved.

引用

页码：372 / 379

页数：8

共 28 条

[21]

Rao KS, 2004, T INDIAN I METALS, V57, P593

[22] Erosion-corrosion of stainless steel under impingement by a fluid jet [J].

Sasaki, K. ;

Burstein, G. T. .

CORROSION SCIENCE, 2007, 49 (01) :92-102

[23] Combined anodic/cathodic transient currents within nucleating pits on Al-Fe alloy surfaces [J].

Speckert, L. ;

Burstein, G. T. .

CORROSION SCIENCE, 2011, 53 (02) :534-539

[24] The metastable pitting behaviors of mild steel in bicarbonate and nitrite solutions containing Cl- [J].

Tang, Y. M. ;

Zuo, Y. ;

Zhao, X. H. .

CORROSION SCIENCE, 2008, 50 (04) :989-994

[25] The metastable pitting of mild steel in bicarbonate solutions [J].

Tang, YM ;

Zuo, Y .

MATERIALS CHEMISTRY AND PHYSICS, 2004, 88 (01) :221-226

[26] THE NUCLEATION, GROWTH AND STABILITY OF MICROPITS IN STAINLESS-STEEL [J].

WILLIAMS, DE ;

STEWART, J ;

BALKWILL, PH .

CORROSION SCIENCE, 1994, 36 (07) :1213-1235

[27] The effect of chloride concentration and pH on pitting corrosion of AA7075 aluminum alloy coated with phenyltrimethoxysilane [J].

Younis, A. A. ;

El-Sabbah, M. M. B. ;

Holze, Rudolf .

JOURNAL OF SOLID STATE ELECTROCHEMISTRY, 2012, 16 (03) :1033-1040

[28]

Zamaletdinov I.J., 2007, PROT MET, V43, P515

← 1 2 3 →