Joining phenomena and joint strength of friction welded joint between pure aluminium and low carbon steel

被引:50
作者
Kimura, M. [1 ]
Ishii, H.
Kusaka, M. [1 ]
Kaizu, K. [1 ]
Fuji, A. [2 ]
机构
[1] Univ Hyogo, Grad Sch Engn, Dept Mech & Syst Engn, Himeji, Hyogo 6712280, Japan
[2] Natl Univ Corp, Kitami Inst Technol, Dept Mech Engn, Kitami, Hokkaido 0908507, Japan
关键词
Friction welding; Pure aluminium; Low carbon steel; Joint efficiency; Intermetallic compound; Forge pressure; Bauschinger effect; MECHANICAL-PROPERTIES; WELDING CONDITIONS; INTERLAYER GROWTH; STAGE;
D O I
10.1179/136217109X425856
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
This paper describes the joining phenomena and joint strength of friction welded joints between pure aluminium (P-Al) and low carbon steel friction welds. When the joint was made at a friction pressure of 30 MPa with a friction speed of 27.5 s(-1), the upsetting (deformation) occurred at the P-Al base metal. P-Al transferred to the half radius region of the weld interface on the low carbon steel side, and then it transferred toward the entire weld interface. When the joint was made at a friction time of 0.9 s, i.e. just after the initial peak of the friction torque, it had similar to 93% joint efficiency and fractured on the P-Al side. This joint had no intermetallic compound at the weld interface. Then, the joint efficiency slightly decreased with increasing friction time. The joint had a small amount of intermetallic compound at the peripheral region of the weld interface when it was made at a friction time of 2.0 s. When the joint was made at a friction time of 0.9 s, the joint efficiency decreased with increasing forge pressure, and all joints were fractured at the P-Al side. Although the joint by forge pressure of 90 MPa had hardly softened region, it had similar to 83% joint efficiency. To clarify the fact of decreasing joint efficiency, the tensile strength of the P-Al base metal at room temperature was investigated, and the tensile test was carried out after various compression stresses and temperatures. The tensile strength of the P-Al base metal has decreased with increasing compression stress at any temperature. Hence, the fact that the joint did not achieve 100% joint efficiency was due to the decrease in the tensile strength of the P-Al base metal by the Bauschinger effect. To obtain higher joint efficiency and fracture on the P-Al side, the joint should be made without higher forge pressure, and with the friction time at which the friction torque reaches the initial peak.
引用
收藏
页码:388 / 395
页数:8
相关论文
共 37 条
[1]  
*AM WELD SOC, 1991, WELD HDB, V2, P750
[2]  
ARITOSHI M, 1988, Q J JPN WELD SOC, V6, P16
[3]  
Dawson RJC, 1983, WELD RES COUNC B, V287, P1
[4]  
Elliott S, 1981, MET CONSTR-BRIT WELD, V13, P221
[5]   Interlayer growth at interfaces of Ti/Al-1%Mn, Ti/Al-4.6%Mg and Ti/pure Al friction weld joints by post-weld heat treatment [J].
Fuji, A ;
Ikeuchi, K ;
Sato, YS ;
Kokawa, H .
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2004, 9 (06) :507-512
[6]   In situ observation of interlayer growth during heat treatment of friction weld joint between pure titanium and pure aluminium [J].
Fuji, A .
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2002, 7 (06) :413-416
[7]   Properties of as welded and heat treated pure titanium-7075 Al-Zn-Mg alloy friction weld joints [J].
Fuji, A ;
Ameyama, K ;
Kokawa, H ;
Satoh, Y ;
North, TH .
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2001, 6 (01) :23-30
[8]  
Futamata M., 1989, Q J JPN WELD SOC, V7, P432
[9]   Effect of friction welding conditions on mechanical properties of A5052 aluminium alloy friction welded joint [J].
Kimura, M ;
Choji, M ;
Kusaka, M ;
Seo, K ;
Fuji, A .
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2006, 11 (02) :209-215
[10]   Joining phenomena during friction stage of A7075-T6 aluminium alloy friction weld [J].
Kimura, M ;
Kusaka, M ;
Seo, K ;
Fuji, A .
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2005, 10 (03) :378-383