Temperature-sensitive mechanical properties of GFRP composites in longitudinal and transverse directions: A comparative study

被引：35

作者：

Manalo, Allan ^{[1
]}

Maranan, Ginghis ^{[1
]}

Sharma, Sukrant ^{[1
]}

Karunasena, Warna ^{[1
]}

Bai, Yu ^{[2
]}

机构：

[1] Univ Southern Queensland, Fac Hlth Engn & Sci, Sch Civil Engn & Surveying, CFM, Toowoomba, Qld 4350, Australia

[2] Monash Univ, Dept Civil Engn, Clayton, Vic, Australia

来源：

COMPOSITE STRUCTURES | 2017年 / 173卷

关键词：

Interlaminar shear; Flexure; Elevated temperature; Longitudinal direction; Transverse direction; Comparative study; TRANSITION-TEMPERATURES; BEHAVIOR; STIFFNESS; PROFILES; FAILURE;

D O I：

10.1016/j.compstruct.2017.04.040

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

A comparative study was conducted to evaluate the temperature-sensitive mechanical properties of glass fibre reinforced polymer (GFRP) composites in the longitudinal and transverse directions. GFRP coupons with different shear span-to-depth ratios were tested under three-point static bending test at temperatures ranging from room temperature up to 200 degrees C. Timoshenko Beam Theory-based procedure was then adopted to calculate the flexural and shear moduli of the GFRP laminates under moderate and elevated in-service temperatures. The results showed that the mechanical properties of the transversely cut specimens is affected more by the increase in temperature than the longitudinally cut specimens. Similarly, the interlaminar shear and flexural strengths of GFRP composites were found influenced more by elevated temperature compared to the stiffness properties. Moreover, the shear modulus undergone more severe degradation compared to the flexural modulus. Simplified empirical models were proposed to estimate the mechanical properties of the GFRP pultruded laminates in both the longitudinal and transverse directions at varying temperatures. (C) 2017 Elsevier Ltd. All rights reserved.

引用

页码：255 / 267

页数：13

共 32 条

[1]

[Anonymous], 1996, ISO 1172:1996

[2]

[Anonymous], D792 ASTM

[3]

*ASTM INT, 2015, D790 ASTM

[4] Experimental investigations on temperature-dependent thermo-physical and mechanical properties of pultruded GFRP composites [J].

Bai, Yu ;

Post, Nathan L. ;

Lesko, John J. ;

Keller, Thomas .

THERMOCHIMICA ACTA, 2008, 469 (1-2) :28-35

[5] Delamination and kink-band failure of pultruded GFRP laminates under elevated temperatures and compression [J].

Bai, Yu ;

Keller, Thomas .

COMPOSITE STRUCTURES, 2011, 93 (02) :843-849

[6] Modeling of stiffness of FRP composites under elevated and high temperatures [J].

Bai, Yu ;

Keller, Thomas ;

Vallee, Till .

COMPOSITES SCIENCE AND TECHNOLOGY, 2008, 68 (15-16) :3099-3106

[7]

BANK LC, 1989, J TEST EVAL, V17, P40, DOI 10.1520/JTE11531J

[8] Determining the elastic interlaminar shear modulus of composite laminates [J].

Chan, A. ;

Chiu, W. K. ;

Liu, X. L. .

COMPOSITE STRUCTURES, 2007, 80 (03) :396-408

[9] A review of the fire behaviour of pultruded GFRP structural profiles for civil engineering applications [J].

Correia, Joao R. ;

Bai, Yu ;

Keller, Thomas .

COMPOSITE STRUCTURES, 2015, 127 :267-287

[10] Mechanical behaviour of pultruded glass fibre reinforced polymer composites at elevated temperature: Experiments and model assessment [J].

Correia, Joao R. ;

Gomes, Marco M. ;

Pires, Jose M. ;

Branco, Fernando A. .

COMPOSITE STRUCTURES, 2013, 98 :303-313

← 1 2 3 4 →