Effect of ultrasonic melt treatment on the refinement of primary Al3Ti intermetallic in an Al-0.4Ti alloy

被引:64
作者
Wang, Feng [1 ]
Eskin, Dmitry [1 ,2 ]
Connolley, Thomas [3 ]
Mi, Jiawei [4 ]
机构
[1] Brunel Univ London, Brunel Ctr Adv Solidificat Technol, London UB8 3PH, Middx, England
[2] Tomsk State Univ, Tomsk 634050, Russia
[3] Diamond Light Source Ltd, Didcot OX11 0DE, Oxon, England
[4] Univ Hull, Sch Engn, Kingston Upon Hull HU6 7RX, East Yorkshire, England
基金
英国工程与自然科学研究理事会;
关键词
Crystal morphology; Solidification; Ultrasonic treatment; Growth from melt; Alloys; Intermetallics; INTERPARTICLE COLLISIONS DRIVEN; GRAIN-REFINEMENT; UNDERCOOLED LIQUID; LIGHT ALLOYS; TI ALLOYS; CAVITATION; ALUMINUM; MECHANISM; SOLIDIFICATION; NUCLEATION;
D O I
10.1016/j.jcrysgro.2015.11.034
中图分类号
O7 [晶体学];
学科分类号
0702 ; 070205 ; 0703 ; 080501 ;
摘要
High intensity ultrasonic melt treatment was applied to an Al-0.4 wt% Ti alloy over three selected temperature ranges: 810 to 770 degrees C (above liquidus), 770 to 730 degrees C (across liquidus), and 730 to 690 degrees C (below liquidus). The size and morphology of the primary Al3Ti intermetallic particles were studied by scanning electron microscopy. It was found that the primary Al3Ti intermetallics were refined as a result of ultrasonication over all three temperature ranges and their morphology changed from typical large dendritic plates to small compact tablets. Quenching experiments before and after the ultrasonication were also carried out to capture the high-temperature stage of intermetallic formation. Based on the size and morphology observations, the mechanisms for the refinement of primary Al3Ti intermetallics at different solidification stages are discussed. (C) 2015 The Authors. Published by Elsevier B.V.
引用
收藏
页码:24 / 30
页数:7
相关论文
共 30 条
[1]   THERMO-CALC & DICTRA, computational tools for materials science [J].
Andersson, JO ;
Helander, T ;
Höglund, LH ;
Shi, PF ;
Sundman, B .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2002, 26 (02) :273-312
[2]  
[Anonymous], 1998, HIGH INTENSITY ULTRA
[3]  
[Anonymous], 1998, FUNDAMENTALS SOLIDIF
[4]   On the mechanism of grain refinement in Al-Zr-Ti alloys [J].
Atamanenko, T. V. ;
Eskin, D. G. ;
Sluiter, M. ;
Katgerman, L. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509 (01) :57-60
[5]   Criteria of Grain Refinement Induced by Ultrasonic Melt Treatment of Aluminum Alloys Containing Zr and Ti [J].
Atamanenko, T. V. ;
Eskin, D. G. ;
Zhang, L. ;
Katgerman, L. .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2010, 41A (08) :2056-2066
[6]  
Daams J.L.C., 1991, ATLAS CRYSTAL STRUCT
[7]  
Dantzig J. A., 2009, SOLIDIFICATION
[8]   INTERPARTICLE COLLISIONS DRIVEN BY ULTRASOUND [J].
DOKTYCZ, SJ ;
SUSLICK, KS .
SCIENCE, 1990, 247 (4946) :1067-1069
[9]  
Eskin GeorgyI., 2015, Ultrasonic Treatment of Light Alloy Melts
[10]   CAVITATION MECHANISM OF ULTRASONIC MELT DEGASSING [J].
ESKIN, GI .
ULTRASONICS SONOCHEMISTRY, 1995, 2 (02) :S137-S141