Stress corrosion behavior of scratched Alloy 690TT steam generator tube in chlorine-containing high-temperature pressurized water

被引：8

作者：

Wu, Bin ^{[1
,2
,3
]}

Meng, Fanjiang ^{[1
]}

Zhang, Zhiming ^{[4
]}

Li, Rongbo ^{[1
,3
]}

Ming, Hongliang ^{[2
,3
]}

Wang, Jianqiu ^{[1
,2
,3
,4
]}

Han, En-Hou ^{[2
,3
,4
]}

机构：

[1] Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China

[2] Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang, Peoples R China

[3] Shanghai Nucl Engn Res & Design Inst Ltd Co, Shanghai 200233, Peoples R China

[4] Inst Corros Sci & Technol, Guangzhou, Peoples R China

来源：

MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION | 2022年 / 73卷 / 10期

基金：

中国国家自然科学基金;

关键词：

Alloy; 690TT; chloride ions; high-temperature pressurized water; scratch; stress corrosion cracking; HEAT-AFFECTED ZONE; MICROSTRUCTURAL CHARACTERIZATION; QUANTITATIVE ASSESSMENT; PASSIVITY-DEGRADATION; SECONDARY-SIDE; CRACKING; DEFORMATION; RESISTANCE; SUBMODES; REACTORS;

D O I：

10.1002/maco.202213215

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Alloy 690TT tube samples with six different scratch depths are prepared for immersion test in high-temperature pressurized water containing chloride ions (Cl-) at 300 degrees C. An immersion test with a duration of 1000 h shows that the scratched area with higher scratch depth has higher stress corrosion cracking sensitivity. In chloride-containing solution, Cl- erodes preferentially into the scratched area through the weak sites such as slip bands and deformed grain boundaries, and this process is continuously promoted with the assistance of higher residual strain in this area.

引用

页码：1563 / 1574

页数：12

共 50 条

[41] Surface Oxidation and Subsurface Microstructure Evolution of Alloy 690TT Induced by Partial Slip Fretting Corrosion in High-Temperature Pure Water [J].

Xin, Long ;

Han, Yongming ;

Ling, Ligong ;

Lu, Yonghao ;

Shoji, Tetsuo .

ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2021, 34 (04) :543-554

[42] Effects of dissolved hydrogen on general corrosion behavior and oxide films of alloy 690TT in PWR primary water [J].

Jeon, Soon-Hyeok ;

Lee, Eun-Hee ;

Hur, Do Haeng .

JOURNAL OF NUCLEAR MATERIALS, 2017, 485 :113-121

[43] Effect of the triangular prism dent on stress corrosion cracking behavior of alloy 690TT heat transfer tube in a lead-containing alkaline solution [J].

Ding, Yun ;

Yuan, Sui ;

Wu, Renquan ;

Wei, Shichen ;

Wang, Shuo ;

Xu, Jian ;

Yu, Hongying ;

Sun, Dongbai .

JOURNAL OF NUCLEAR MATERIALS, 2024, 594

[44] Effects of Surface State and Applied Stress on Stress Corrosion Cracking of Alloy 690TT in Lead-containing Caustic Solution [J].

Zhang, Zhiming ;

Wang, Jianqiu ;

Han, En-Hou ;

Ke, Wei .

JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2012, 28 (09) :785-792

[45] Effects of Surface State and Applied Stress on Stress Corrosion Cracking of Alloy 690TT in Lead-containing Caustic Solution [J].

Zhiming Zhang Jianqiu Wang EnHou Han and Wei Ke State Key Laboratory for Corrosion and Protection Institute of Metal Research Chinese Academy of Sciences Shenyang China .

JournalofMaterialsScience&Technology, 2012, 28 (09) :785-792

[46] Trans-twins stress corrosion cracking behaviors of Alloy 690TT in lead-containing caustic solution at 330 °C [J].

Zhang, Z. M. ;

Wang, J. Q. ;

Han, E. -H. ;

Ke, W. .

NUCLEAR ENGINEERING AND DESIGN, 2011, 241 (12) :4944-4952

[47] Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steelin Pure Water [J].

XingChen Liu ;

HongLiang Ming ;

ZhiMing Zhang ;

JianQiu Wang ;

LiChen Tang ;

Hao Qian ;

YongCheng Xie ;

EnHou Han .

Acta Metallurgica Sinica(English Letters), 2019, 32 (12) :1437-1448

[48] The role of frequency on fretting corrosion of Alloy 690TT against 304 stainless steel in high temperature high pressure water [J].

Xin, L. ;

Lu, Y. H. ;

Otsuka, Y. ;

Mutoh, Y. ;

Wang, Z. H. ;

Shoji, T. .

MATERIALS CHARACTERIZATION, 2017, 134 :260-273

[49] Crevice Corrosion Behavior of Alloy 690 in High-Temperature Aerated Chloride Solution [J].

Ning, Fangqiang ;

Tan, Jibo ;

Zhang, Ziyu ;

Wang, Xiang ;

Wu, Xinqiang ;

Han, En-Hou ;

Ke, Wei .

MATERIALS, 2022, 15 (15)

[50] Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steel in Pure Water [J].

Liu, Xing-Chen ;

Ming, Hong-Liang ;

Zhang, Zhi-Ming ;

Wang, Jian-Qiu ;

Tang, Li-Chen ;

Qian, Hao ;

Xie, Yong-Cheng ;

Han, En-Hou .

ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2019, 32 (12) :1437-1448

← 1 2 3 4 5 →