Characterizations of 21-4N to 4Cr9Si2 stainless steel dissimilar joint bonded by electric-resistance-heat-aided friction welding

被引:29
作者
Li, Wen-Ya [1 ]
Yu, Min [1 ]
Li, Jinglong [1 ]
Zhang, Guifeng [2 ]
Wang, Shiyuan [2 ]
机构
[1] NW Polytech Univ, Shaanxi Key Lab Frict Welding Technol, Xian 710072, Shaanxi, Peoples R China
[2] Xi An Jiao Tong Univ, Sch Mat Sci & Engn, Xian 710049, Shaanxi, Peoples R China
关键词
Electric-resistance-heat-aided friction welding; Stainless steel; Secondary friction surface; Microstructure; Microhardness; SHEETS; CARBON; COPPER; SPEED;
D O I
10.1016/j.matdes.2009.04.032
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A new welding process, electric-resistance-heat-aided friction welding (ERHAFW), was introduced in this study. To further improve the joint quality and energy-saving, electric resistance welding was combined with the conventional continuous-drive friction welding. 21-4N (austenitic stainless steel) and 4Cr9Si2 (martensitic stainless steel) valve steel rods of 4 mm diameter were used as base metals. The results show that electric-resistance-heat-aided friction welding can be applied to join thin rods within a relatively short time, which is very difficult for conventional friction welding (FW). The microstructure of ERHAFW bonded 21-4N to 4Cr9Si2 presents non-uniform across the joint. Different structure zones are observed from the weld line to both sides, which are the weld center. thermo-mechanically affected zone (TMAZ) and heat affected zone (HAZ). These regions exhibit different structures owing to the difference in the thermophysical and mechanical properties of these two steels under the fast heating and cooling during welding. The variation of microhardness in the joint is attributed to the microstructure change. The higher microhardness is obtained in the weld center and TMAZ of 4Cr9Si2 corresponding to the presence of fine tempered martensite and carbides. (C) 2009 Elsevier Ltd. All rights reserved.
引用
收藏
页码:4230 / 4235
页数:6
相关论文
共 27 条
[1]  
AFES H, 2007, MAT DESIGN, V28, P948
[2]  
CHEN HC, 1994, T CHINA WELD I, V15, P248
[3]  
Chen Luo-sheng, 2008, Shengwu Jiagong Guocheng, V6, P58
[4]  
CUI ZQ, 1989, METALLOGRAPHY HEAT T
[5]  
DOBROVIDOV AN, 1975, WELD PROD+, V22, P22
[6]  
Hazlett, 1962, WELD J, V41, p448s
[7]  
HAZLETT TH, 1962, WELD J, V41, pS49
[8]   Real time monitoring weld quality of resistance spot welding for the fabrication of sheet metal assemblies [J].
Jou, M .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2003, 132 (1-3) :102-113
[9]   The influence of welding parameters on the joint strength of resistance spot-welded titanium sheets [J].
Kahraman, Nizamettin .
MATERIALS & DESIGN, 2007, 28 (02) :420-427
[10]   Fatigue properties of inertia dissimilar friction-welded stainless steels [J].
Lee, DG ;
Jang, KC ;
Kuk, JM ;
Kim, IS .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2004, 155 :1402-1407