Evaluation of stress corrosion cracking phenomenon in an AISI type 316LN stainless steel using acoustic emission technique

被引:66
作者
Shaikh, H. [1 ]
Amirthalingam, R.
Anita, T.
Sivaibharasi, N.
Jaykurnar, T.
Manohar, P.
Khatak, H. S.
机构
[1] Indira Gandhi Ctr Atom Res, Corros Sci & Technol Div, Kalpakkam 603102, Tamil Nadu, India
[2] Govt Arts Coll, Dept Phys, Cuddalore, Tamil Nadu, India
[3] Indira Gandhi Ctr Atom Res, Non Destruct Evaluat Div, Kalpakkam 603102, Tamil Nadu, India
[4] Madras Inst Technol, Dept Appl Sci & Humanities, Madras, Tamil Nadu, India
关键词
stress corrosion cracking;
D O I
10.1016/j.corsci.2006.06.007
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
This paper deals with the analysis of the acoustic emission (AE) signals to determine the microprocess during stress corrosion cracking (SCC) of AISI type 316LN stainless steel that cause the AE, and thus the mechanism of the SCC process. AE with amplitudes ranging from 27.6 to 46.5 dB with different counts, energy and rise times occurred during SCC of type 316LN stainless steel in 45% MgCl2 at 413 K. The analysis of the AE signals in conjunction with fractography indicated that a surge in the AE counts and energy indicated initiation of SCC. AE was found to be continuous prior to the initiation. The time gap between AE events increased during initiation. AE events occurred in bursts during crack growth. Plastic deformation ahead of the crack tip was determined to be the major source of AE during propagation of SCC in type 316LN stainless steel. The cracking was found to initiate and propagate in the transgranular mode. (c) 2006 Elsevier Ltd. All rights reserved.
引用
收藏
页码:740 / 765
页数:26
相关论文
共 57 条
[31]  
MUKAI Y, 1978, ASTM STP, V645
[32]   Acoustic emission from tensile deformation of unnotched and notched specimens of AISI type 304 stainless steels [J].
Mukhopadhyay, CK ;
Ray, KK ;
Jayakumar, T ;
Raj, B .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 255 (1-2) :98-106
[33]  
MURALEEDHARAN P, 1993, THESIS U MADRAS MADR, P98
[34]   DIRECT OBSERVATIONS OF STRESS-CORROSION CRACK TIPS OF TYPE-304 STAINLESS-STEEL IN A BOILING 42-PERCENT MGCL2 SOLUTION [J].
NAKAYAMA, T ;
TAKANO, M .
CORROSION, 1981, 37 (04) :226-231
[35]  
Nozue A., 1982, J ACOUSTIC EMISSION, V1, P1
[36]   TRANSITION OF CRACKING MECHANISMS FROM ACTIVE PATH CORROSION TO HYDROGEN EMBRITTLEMENT IN HIGH-STRENGTH STEELS IN A BOILING NITRATE SOLUTION [J].
OKADA, H ;
YUKAWA, KI ;
TAMURA, H .
CORROSION, 1976, 32 (05) :201-203
[37]   APPLICATION OF ACOUSTIC-EMISSION TECHNIQUE TO STUDY OF STRESS-CORROSION CRACKING IN DISTINGUISHING BETWEEN ACTIVE PATH CORROSION AND HYDROGEN EMBRITTLEMENT [J].
OKADA, H ;
YUKAWA, KI ;
TAMURA, H .
CORROSION, 1974, 30 (07) :253-255
[38]   INFLUENCE OF PRIOR DEFORMATION ON THE SENSITIZATION OF AISI TYPE 316LN STAINLESS-STEEL [J].
PARVATHAVARTHINI, N ;
DAYAL, RK ;
GNANAMOORTHY, JB .
JOURNAL OF NUCLEAR MATERIALS, 1994, 208 (03) :251-258
[39]  
POLLOCK AA, 1986, ASTM STP, V908
[40]   ACOUSTIC-EMISSION METHOD FOR MONITORING CORROSION REACTIONS [J].
RETTIG, TW ;
FELSEN, MJ .
CORROSION, 1976, 32 (04) :121-126