Oxidation and hot corrosion behaviors of Nb-Si based ultrahigh temperature alloys at 900 °C

被引：20

作者：

He, Jia-hua ^{[1
]}

Guo, Xi-ping ^{[1
]}

Qiao, Yan-qiang ^{[1
]}

机构：

[1] Northwestern Polytech Univ, State Key Lab Solidificat Proc, Xian 710072, Peoples R China

来源：

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2021年 / 31卷 / 01期

基金：

中国国家自然科学基金; 国家重点研发计划;

关键词：

Nb-Si based alloys; molten salts; oxidation; hot corrosion; silicate; MICROSTRUCTURE; TI; CHLORIDE;

D O I：

10.1016/S1003-6326(20)65488-7

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Oxidation and hot corrosion behaviors at 900 degrees C of Nb-Si based ultrahigh temperature alloys were investigated. Both oxidation and hot corrosion kinetics curves of the alloy involve an initial parabolic stage and a later rapid linear stage. In the initial oxidation stage (1-50 h), a thin and continuous scale is formed on the alloy surface, while severe pest degradation phenomenon is observed in the linear oxidation stage. Compared with oxidation of the alloy in static air, a linear hot corrosion stage happens earlier and catastrophic scale disintegration occurs after hot corrosion for 20-100 h, demonstrating that molten salts (Na2SO4 and NaCl) could significantly accelerate the oxidation process of the alloy. STEM results indicate that the corroded scale consists mainly of TiO2, Nb2O5, TiNb2O7, amorphous silicate and NaNbO3.

引用

页码：207 / 221

页数：15

共 32 条

[1] Preparation and hot corrosion behaviour of an Al-gradient NiCoCrAlYSiB coating on a Ni-base superalloy [J].

Bao, Z. B. ;

Wang, Q. M. ;

Li, W. Z. ;

Liu, X. ;

Gong, J. ;

Xiong, T. Y. ;

Sun, C. .

CORROSION SCIENCE, 2009, 51 (04) :860-867

[2] The balance of mechanical and environmental properties of a multielement niobium-niobium silicide-based in situ composite [J].

Bewlay, BP ;

Jackson, MR ;

Lipsitt, HA .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (12) :3801-3808

[3]

Birks N, 2006, INTRODUCTION TO THE HIGH-TEMPERATURE OXIDATION OF METALS, 2ND EDITION, P1, DOI 10.1017/CBO9781139163903

[4] The influence of the reactive element yttrium on the stress in alumina scales formed by oxidation [J].

Christensen, RJ ;

Tolpygo, VK ;

Clarke, DR .

ACTA MATERIALIA, 1997, 45 (04) :1761-1766

[5] The effect of Nb and Si on the hot corrosion behaviors of TiAl coatings on a Ti-6Al-4V alloy [J].

Dai, Jingjie ;

Zhang, Hongxia ;

Sun, Caixia ;

Li, Shouying ;

Chen, Chuanzhong ;

Yang, Yong .

CORROSION SCIENCE, 2020, 168

[6] THE THERMAL EXPANSION OF NIOBIUM PENTOXIDE AND ITS EFFECT ON THE SPALLING OF NIOBIUM OXIDATION FILMS [J].

DOUGLASS, DL .

JOURNAL OF THE LESS-COMMON METALS, 1963, 5 (02) :151-157

[7] Hot corrosion in gas turbine components [J].

Eliaz, N ;

Shemesh, G ;

Latanision, RM .

ENGINEERING FAILURE ANALYSIS, 2002, 9 (01) :31-43

[8] Hot corrosion behavior of NbSi2/SiO2-Nb2O5 multilayer coating on Nb alloy [J].

Ge, Yulin ;

Wang, Yaming ;

Chen, Junchen ;

Zou, Yongchun ;

Guo, Lixin ;

Ouyang, Jiahu ;

Jia, Dechang ;

Zhou, Yu .

JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 767 :7-15

[9] A study of the microstructures and oxidation of Nb-Si-Cr-Al-Mo in situ composites alloyed with Ti, Hf and Sn [J].

Geng, Jie ;

Tsakiropoulos, Panos .

INTERMETALLICS, 2007, 15 (03) :382-395

[10] THE EFFECTS OF CHLORIDES, HYDROGEN-CHLORIDE, AND SULFUR-DIOXIDE IN THE OXIDATION OF STEELS BELOW DEPOSITS [J].

GRABKE, HJ ;

REESE, E ;

SPIEGEL, M .

CORROSION SCIENCE, 1995, 37 (07) :1023-1043

← 1 2 3 4 →