Hydride Reorientation and Delayed Hydride Cracking of Spent Fuel Rods in Dry Storage

被引:4
作者
Kim, Young S. [1 ]
机构
[1] Korea Atom Energy Res Inst, Nucl Mat Res Div, Taejon 305353, South Korea
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2009年 / 40A卷 / 12期
关键词
PRESSURE TUBE MATERIAL; ZIRCONIUM ALLOYS; TERMINAL SOLUBILITY; HYDROGEN; PRECIPITATION; TEMPERATURE; STRESS; DISSOLUTION; OXIDATION; BEHAVIOR;
D O I
10.1007/s11661-009-0044-6
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The aim of this work is to investigate the effect of thermal creep during vacuum drying of spent fuel rods on hydride reorientation and their delayed hydride cracking (DHC) susceptibility. To these ends, we analyzed Tsai's thermal creep results of irradiated Zircaloy-4 cladding segments from two pressurized water reactors and Simpson and Ells' observation where zirconium alloy cladding tube failed during long-term storage at room temperature. On cooling under 190 MPa, the spent fuel rods crept to 3.5 pct strain during vacuum drying showed large radial hydrides, while the ones crept to 0.35 pct strain had very fine radial hydrides. Thus, it is suggested that prior creep deformation promotes hydride reorientation in spent fuel rods on cooling after vacuum drying. Evidence for this suggestion is provided by a model experiment. Considering Kim's DHC model and experimental facts showing precipitation of hydrides even at room temperature at stress raisers, we suggest that spent fuel rods would fail by DHC in dry storage if stress raisers are present inside the cladding on cooling to below 180 degrees C, and then axial splits of the failed spent fuel rods would occur by DHC due to fuel expansion by UO2 oxidation.
引用
收藏
页码:2867 / 2875
页数:9
相关论文
共 38 条
[1]  
Ambler J., 1984, ASTM STP, V824, P653
[2]  
[Anonymous], 1989, ZIRC NUCL IND 8 INT, DOI DOI 10.1520/STP18858S
[3]  
AOMI M, 2008, J ASTM INT, V5
[4]  
BIRNBAUM HK, 1976, J LESS-COMMON MET, V49, P357, DOI 10.1016/0022-5088(76)90048-5
[5]   METALLOGRAPHIC STUDY OF THE TERMINAL SOLUBILITY OF HYDROGEN IN ZIRCONIUM AT LOW HYDROGEN CONCENTRATIONS [J].
CANN, CD ;
ATRENS, A .
JOURNAL OF NUCLEAR MATERIALS, 1980, 88 (01) :42-50
[6]   INSITU STUDY OF DISSOLUTION OF GAMMA-ZIRCONIUM HYDRIDE IN ZIRCONIUM [J].
CARPENTER, GJC ;
WATTERS, JF .
JOURNAL OF NUCLEAR MATERIALS, 1978, 73 (02) :190-197
[7]   CRACK INITIATION AT LONG RADIAL HYDRIDES IN ZR-2.5NB PRESSURE TUBE MATERIAL AT ELEVATED-TEMPERATURES [J].
CHOUBEY, R ;
PULS, MP .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1994, 25 (05) :993-1004
[8]  
Cunningham M. E., 1987, PNL6364
[9]   EFFECT OF STRESS ON HYDRIDE PRECIPITATION IN ZIRCONIUM-2.5-PERCENT NIOBIUM AND ON DELAYED HYDRIDE CRACKING [J].
EADIE, RL ;
COLEMAN, CE .
SCRIPTA METALLURGICA, 1989, 23 (11) :1865-1870
[10]  
Einziger R. E., 2005, Radwaste Solutions, V12, P44