Room-temperature synthesis of tin oxide nano-electrodes in aqueous solutions

被引：17

作者：

Masuda, Yoshitake ^{[1
]}

Ohji, Tatsuki ^{[1
]}

Kato, Kazumi ^{[1
]}

机构：

[1] Natl Inst Adv Ind Sci & Technol, Moriyama Ku, Nagoya, Aichi 4638560, Japan

来源：

THIN SOLID FILMS | 2009年 / 518卷 / 02期

关键词：

Tin oxide; Nanocrystal; Morphology control; Room-temperature synthesis; Aqueous synthesis; Liquid phase crystal deposition; Molecular-sensor; THIN-FILM; SNO2; NANORIBBONS; NANOBELTS; NANOTUBES; GROWTH;

D O I：

10.1016/j.tsf.2009.07.102

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Tin oxide nano-electrodes were fabricated on fluorine doped tin oxide (FTO) substrates at room temperature. SnO(2) was crystallized from ions in aqueous solutions to cover the substrates uniformly. They were single phase of SnO(2) nano-crystals and about 5-10 nm in size. The surface coatings changed the surface morphology of FTO substrates to increase roughness and surface area. FTO substrates covered with tin oxide had the same transparency as bare IFTO substrates in the range from 200 nm to 850 nm. (C) 2009 Elsevier B.V. All rights reserved.

引用

页码：850 / 852

页数：3

共 22 条

[1]

Baes C. F., 1976, HYDROLYSIS CATIONS

[2] Tin oxide nanowires, nanoribbons, and nanotubes [J].

Dai, ZR ;

Gole, JL ;

Stout, JD ;

Wang, ZL .

JOURNAL OF PHYSICAL CHEMISTRY B, 2002, 106 (06) :1274-1279

[3] Single crystal SnO2 zigzag nanobelts [J].

Duan, JH ;

Yang, SG ;

Liu, HW ;

Gong, JF ;

Huang, HB ;

Zhao, XN ;

Zhang, R ;

Du, YW .

JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 2005, 127 (17) :6180-6181

[4] Transparent conducting oxides [J].

Ginley, DS ;

Bright, C .

MRS BULLETIN, 2000, 25 (08) :15-18

[5] Nanotubular SnO2 templated by cellulose fibers:: Synthesis and gas sensing [J].

Huang, J ;

Matsunaga, N ;

Shimanoe, K ;

Yamazoe, N ;

Kunitake, T .

CHEMISTRY OF MATERIALS, 2005, 17 (13) :3513-3518

[6] Synthesis of SnO2 nanoparticles through the controlled precipitation route [J].

Ibarguen, C. Ararat ;

Mosquera, A. ;

Parra, R. ;

Castro, M. S. ;

Rodriguez-Paez, J. E. .

MATERIALS CHEMISTRY AND PHYSICS, 2007, 101 (2-3) :433-440

[7] Tin-based amorphous oxide: A high-capacity lithium-ion-storage material [J].

Idota, Y ;

Kubota, T ;

Matsufuji, A ;

Maekawa, Y ;

Miyasaka, T .

SCIENCE, 1997, 276 (5317) :1395-1397

[8] Growth of aligned square-shaped SnO2 tube arrays [J].

Liu, Y ;

Liu, M .

ADVANCED FUNCTIONAL MATERIALS, 2005, 15 (01) :57-62

[9]

Liu YK, 2001, ADV MATER, V13, P1883, DOI 10.1002/1521-4095(200112)13:24<1883::AID-ADMA1883>3.0.CO

[10]

2-Q

← 1 2 3 →