Mechanochemical synthesis of anatase and rutile nanopowders from TiOSO4

被引：41
作者：
Billik, P. [1 ]
Plesch, G. [1 ]
机构：
[1] Comenius Univ Mlynska Dolina, Fac Nat Sci, Dept Inorgan Chem, Bratislava 84215, Slovakia
来源：
MATERIALS LETTERS | 2007年 / 61卷 / 4-5期
关键词：
mcchanochemical synthesis; TiO2; anatase; rutile; nanomaterials;
D O I：
10.1016/j.matlet.2006.06.080
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The synthesis of titanium dioxide phases rutile and anatase via mechanochemical reaction and subsequent annealing of the products was studied. TiOSO4-xH(2)O and anhydrous Na2CO3 Powders in the molar ratio 1: 1 were used as starting reactants. The Na2SO4-xH(2)O by-product was removed by simple water washing process. The synthesis of nanocrystalline rutile is almost complete after 60 min milling and particles with average size of 15 nm were obtained. Nanoparticles of anatase with average size of 5-35 nm were obtained after 5 min milling and subsequent annealing at 300-600 degrees C. (c) 2006 Elsevier B.V All rights reserved.
引用
收藏
页码：1183 / 1186
页数：4
相关论文
共 24 条
  • [1] Visible-light photocatalysis in nitrogen-doped titanium oxides
    Asahi, R
    Morikawa, T
    Ohwaki, T
    Aoki, K
    Taga, Y
    [J]. SCIENCE, 2001, 293 (5528) : 269 - 271
  • [2] Avvakumov E., 2001, SOFT MECHANOCHEMICAL, P2
  • [3] Mechanochemical route for sulphide nanoparticles preparation
    Baláz, P
    Boldizárová, E
    Godocíková, E
    Briacin, J
    [J]. MATERIALS LETTERS, 2003, 57 (9-10) : 1585 - 1589
  • [4] Kinetics and mechanisms of phase transformations induced by ball-milling in anatase TiO2
    Bégin-Colin, S
    Girot, T
    Le Caër, G
    Mocellin, A
    [J]. JOURNAL OF SOLID STATE CHEMISTRY, 2000, 149 (01) : 41 - 48
  • [5] Hydrothermal reactions under mechanochemical action
    Boldyrev, VV
    [J]. POWDER TECHNOLOGY, 2002, 122 (2-3) : 247 - 254
  • [6] BREZOVA V, 2006, UNPUB P C ENV APPL A
  • [7] Syntheses of TiO2 photocatalysts by the molten salts method application to the photocatalytic degradation of Prosulfuron®
    Docters, T
    Chovelon, JM
    Herrmann, JM
    Deloume, JP
    [J]. APPLIED CATALYSIS B-ENVIRONMENTAL, 2004, 50 (04) : 219 - 226
  • [8] Nanocrystalline zirconia powders synthesised by mechanochemical processing
    Dodd, AC
    Tsuzuki, T
    McCormick, PG
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 301 (01): : 54 - 58
  • [9] LIGHT-INDUCED REDOX REACTIONS IN NANOCRYSTALLINE SYSTEMS
    HAGFELDT, A
    GRATZEL, M
    [J]. CHEMICAL REVIEWS, 1995, 95 (01) : 49 - 68
  • [10] Modification of the physicochemical properties of commercial TiO2 samples by soft mechanical activation
    Hidalgo, MC
    Colón, G
    Navío, JA
    [J]. JOURNAL OF PHOTOCHEMISTRY AND PHOTOBIOLOGY A-CHEMISTRY, 2002, 148 (1-3) : 341 - 348
123