Oxidation behavior of silicide coating on Ti3SiC2-based ceramic

被引：13

作者：

Liu, GM ^{[1
]}

Li, MS ^{[1
]}

Zhou, YC ^{[1
]}

Zhang, YM ^{[1
]}

机构：

[1] Chinese Acad Sci, Met Res Inst, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China

来源：

MATERIALS RESEARCH INNOVATIONS | 2002年 / 6卷 / 5-6期

关键词：

titanium silicon carbide; silicide coating; Oxidation Oxide scale;

D O I：

10.1007/s10019-002-0201-7

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A silicide coating was prepared on Ti3SiC2-based ceramic by pack cementation to improve the oxidation resistance of Ti3SiC2, which is a technologically important material for high temperature applications. The microstructure, phase composition and oxidation resistance of the coated sample were investigated. The results demonstrated that the silicide coating was mainly composed of TiSi2 and SiC. A single layer of a mixture of SiO2 and TiO2 was formed on the surface of the coated sample during isothermal oxidation at 1100 degreesC and 1200 degreesC for 20h. Compared to Ti3SiC2, the parabolic rate constant of silicide coated Ti3SiC2 decreased by 2similar to3 orders of magnitude. Furthermore, the coated sample showed much better cyclic oxidation resistance than Ti3SiC2 during the cyclic oxidation at 1100 degreesC for 400 times. However, during the preparation of the coating, a number of fine cracks formed in the outer layer of the coating. When these cracks penetrated the whole coating during the cyclic oxidation, the oxidation rate was accelerated, which degraded the oxidation resistance.

引用

页码：226 / 231

页数：6

共 15 条

[1] Synthesis and characterization of a remarkable ceramic: Ti3SiC2 [J].

Barsoum, MW ;

ElRaghy, T .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1996, 79 (07) :1953-1956

[2] Diffusion kinetics of the carburization and silicidation of Ti3SiC2 [J].

El-Raghy, T ;

Barsoum, MW .

JOURNAL OF APPLIED PHYSICS, 1998, 83 (01) :112-119

[3]

ElRaghy T, 1997, J AM CERAM SOC, V80, P513, DOI 10.1111/j.1151-2916.1997.tb02861.x

[4] Field-activated pressure-assisted combustion synthesis of polycrystalline Ti3SiC2 [J].

Feng, AG ;

Orling, T ;

Munir, ZA .

JOURNAL OF MATERIALS RESEARCH, 1999, 14 (03) :925-939

[5] Dense Ti3SiC2 prepared by reactive HIP [J].

Gao, NF ;

Miyamoto, Y ;

Zhang, D .

JOURNAL OF MATERIALS SCIENCE, 1999, 34 (18) :4385-4392

[6]

KIM S, 1982, MAT SCI TECH UK, V14, P822

[7]

OKANO T, 1993, T MET SOC JPN A, V14, P597

[8] SOLID-STATE SYNTHESIS AND CHARACTERIZATION OF THE TERNARY PHASE TI3SIC2 [J].

RACAULT, C ;

LANGLAIS, F ;

NASLAIN, R .

JOURNAL OF MATERIALS SCIENCE, 1994, 29 (13) :3384-3392

[9]

SAMSONOV GV, 1982, OXIDE HDB

[10] OXIDATION BEHAVIOR OF TIAL3 COATINGS AND ALLOYS [J].

SMIALEK, JL .

CORROSION SCIENCE, 1993, 35 (5-8) :1199-1208

← 1 2 →