Synthesis process of Mg-Ti BCC alloys by means of ball milling

被引:47
作者
Asano, Kohta [1 ]
Enoki, Hirotoshi [1 ]
Akiba, Etsuo [1 ]
机构
[1] Natl Inst Adv Ind Sci & Technol, Tsukuba, Ibaraki 3058565, Japan
关键词
Magnesium-titanium alloys; BCC phase; Mechanical alloying; Ball milling; Hydrogen storage; HYDROGEN STORAGE PROPERTIES; CLOSE-PACKED METALS; CR-MO ALLOYS; SOLID-SOLUTION; CRYSTAL-STRUCTURE; HCP METALS; PHASE-STABILITY; HYDRIDES; TITANIUM; FCC;
D O I
10.1016/j.jallcom.2009.06.140
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
The synthesis process of Mg-Ti alloys with a BCC (body centered cubic) structure by means of ball milling was studied by X-ray diffraction and various microscopic techniques. The morphology and crystal structure of Mg-Ti alloys changed with increase of milling time. During ball milling of Mg and Ti powders in molar ratio of 1:1, firstly, plate-like particles stuck on the surface of the milling pot and balls. After these plate-like particles fell off from the surface of the milling pot and balls, spherical particles with the mean diameter of 1 mm, in which concentric layers of Mg and Ti were disposed, were formed. These spherical particles were crushed into spherical particles with the diameter of around 10 mu m by introduction of cracks along the boundaries between Mg and Ti layers. Finally, the Mg50Ti50 BCC phase with the lattice parameter of a = 0.342(1) nm and the grain size of 3 nm was formed. During milling of Mg and Ti to synthesize the BCC alloy, Mg and Ti were deformed mainly by the basal plane slip and the twinning deformation, respectively. Ti acted as abrasives for Mg which had stuck on the surface of the milling pot and balls. The BCC phase was found after Mg dissolved in Ti. (C) 2009 Elsevier B.V. All rights reserved.
引用
收藏
页码:115 / 123
页数:9
相关论文
共 50 条
  • [1] Phase stability change with Zr content in β-type Ti-Nb alloys
    Abdel-Hady, Mohamed
    Fuwa, Hiroki
    Hinoshita, Keita
    Kimura, Haruka
    Shinzato, Yoshifumi
    Morinaga, Masahiko
    [J]. SCRIPTA MATERIALIA, 2007, 57 (11) : 1000 - 1003
  • [2] General approach to phase stability and elastic properties of β-type Ti-alloys using electronic parameters
    Abdel-Hady, Mohamed
    Hinoshita, Keita
    Morinaga, Masahiko
    [J]. SCRIPTA MATERIALIA, 2006, 55 (05) : 477 - 480
  • [3] Hydrogen absorption by Laves phase related BCC solid solution
    Akiba, E
    Iba, H
    [J]. INTERMETALLICS, 1998, 6 (06) : 461 - 470
  • [4] Crystal structural studies of AB5-type, BCC and Zint1 phase hydrogen absorbing alloys
    Akiba, E
    Enoki, H
    Nakamura, Y
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 329 : 321 - 324
  • [5] Metallic hydrides III: Body-centered-cubic solid-solution alloys
    Akiba, E
    Okada, M
    [J]. MRS BULLETIN, 2002, 27 (09) : 699 - 703
  • [6] Non-basal slip in magnesium-lithium alloy single crystals
    Ando, S
    Tonda, H
    [J]. MATERIALS TRANSACTIONS JIM, 2000, 41 (09): : 1188 - 1191
  • [7] Effect of Li addition on synthesis of Mg-TiBCC alloys by means of ball milling
    Asano, Kohta
    Enoki, Hirotoshi
    Akiba, Etsuo
    [J]. MATERIALS TRANSACTIONS, 2007, 48 (02) : 121 - 126
  • [8] Synthesis of HCP, FCC and BCC structure alloys in the Mg-Ti binary system by means of ball milling
    Asano, Kohta
    Enoki, Hirotoshi
    Akiba, Etsuo
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 480 (02) : 558 - 563
  • [9] Synthesis of Mg-Ti FCC hydrides from Mg-Ti BCC alloys
    Asano, Kohta
    Enoki, Hirotoshi
    Akiba, Etsuo
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 478 (1-2) : 117 - 120
  • [10] Texture evolution during grain growth in recrystallized commercially pure titanium
    Bozzolo, N
    Dewobroto, N
    Grosdidier, T
    Wagner, E
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 397 (1-2): : 346 - 355