Oxidation behavior of Alloy 718 at a high temperature

被引：35
作者：
Geng, Lin
Na, Young-Sang
Park, Nho-Kwang
机构：
[1] Korea Inst Machinery Mat, Adv Mat Res Div, Mat Res Inst, Chang Won 641010, Kyungnam, South Korea
[2] Harbin Inst Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China
来源：
MATERIALS & DESIGN | 2007年 / 28卷 / 03期
关键词：
Superalloys;
D O I：
10.1016/j.matdes.2005.11.020
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The surface oxidation behavior of Alloy 718 is not well understood due to the chemical complexity of the alloy system. In this work, high temperature oxidation behavior of Alloy 718 in air at 1100 degrees C was investigated by varying the oxidation time up to 180 It. Three distinguished surface layers were observed depending on the oxidation time. Outside layer was single-phase Nb-rich Cr oxides with some voids and microcracks. The second layer had small amount of discontinuous phase (Al2O3). Both outside layer and second layer have often been observed in Ni-based superalloys. The third layer with complicate shapes of carbides was also observed in the present study. It was composed of the various (TixNby)C type carbides showing the different shape with the different ratio of x to y. (c) 2005 Elsevier Ltd. All rights reserved.
引用
收藏
页码：978 / 981
页数：4
相关论文
共 9 条
[1]  
Burke MG., 1991, SUPERALLOYS 718 625, P337, DOI 10.7449/1991/Superalloys_1991_337_350
[2]   INTERACTION BETWEEN OXIDATION AND THERMOMECHANICAL FATIGUE IN IN738LC SUPERALLOY .1. [J].
ESMAEILI, S ;
ENGLERPINTO, CC ;
ILSCHNER, B ;
REZAIARIA, F .
SCRIPTA METALLURGICA ET MATERIALIA, 1995, 32 (11) :1777-1781
[3]  
Gusev A I, 1985, Russ. J. Phys. Chem., V59, P336
[4]  
LORIA EA, 1992, JOM JUN, P33
[5]  
MOON DP, 1989, MATER SCI TECH SER, V5, P754, DOI 10.1179/026708389790222799
[6]  
NIELSEN DR, 1994, SUPERALLOYS 718, 625, 706 AND VARIOUS DERIVATIVES, P373
[7]  
SIMS CT, 1987, SUPERALLOYS, V2, P293
[8]   AN ANALYTICAL ELECTRON-MICROSCOPY STUDY OF THE ROLE OF LA AND Y DURING HIGH-TEMPERATURE OXIDATION OF SELECTED NI-BASE ALLOYS [J].
TAWANCY, HM ;
ABBAS, NM .
SCRIPTA METALLURGICA ET MATERIALIA, 1993, 29 (05) :689-694
[9]  
ZHAO D, 1994, SUPERALLOYS 718, 625, 706 AND VARIOUS DERIVATIVES, P303
1