Low-temperature wetting of sapphire using Sn-Ti active solder alloys

被引:30
作者
Mu, Dekui [1 ]
Feng, Kuiyuan [1 ]
Lin, Qiaoli [2 ]
Huang, Han [3 ]
机构
[1] Huaqiao Univ, Inst Mfg Engn, Fujian Engn Res Ctr Intelligent Mfg Brittle Mat, Xiamen 361021, Fujian, Peoples R China
[2] Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730000, Gansu, Peoples R China
[3] Univ Queensland, Sch Mech & Min Engn, Brisbane, Qld 4072, Australia
基金
中国国家自然科学基金;
关键词
Sapphire; Wettability; Bonding strength; Brazing; BRAZING COPPER; CR ALLOYS; ALUMINA; WETTABILITY; CU; AL2O3; ADSORPTION;
D O I
10.1016/j.ceramint.2019.07.239
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Monocrystalline alumina, known as sapphire, is one of the most commonly used ceramics in electronic devices. Understanding its wettability is thus of great importance for its engineering applications. In this work, the low-temperature wetting mechanisms of Sn-Ti active solder alloy on C-plane sapphire was comprehensively studied using the sessile drop method. The addition of 0.1 wt % Ti was found to effectively improve the wettability of Sn-Ti alloys, and the lowest contact angle on the sapphire substrate was achieved at 950 degrees C when Ti content was increased to 3 wt%. Thermal dynamics analysis and experimental results indicated that the isothermal spreading of Sn-3Ti alloy is controlled by the Ti adsorption in the vicinity of wetting triple line. Moreover, sapphire was successfully brazed using Sn-3Ti alloy at 500, 550, and 600 degrees C, and the maximum shear strength was measured as 30.3 MPa. Our understanding of the wettability of sapphire provides the fundamental theory for developing new bonding technique for this important crystal.
引用
收藏
页码:22175 / 22182
页数:8
相关论文
共 35 条
[1]   Interface phenomena in the B4C/(Me-Ti) systems (Me = Cu, Au and Sn) [J].
Aizenshtein, M ;
Froumin, N ;
Frage, N ;
Dariel, MP .
JOURNAL OF MATERIALS SCIENCE, 2005, 40 (9-10) :2325-2327
[2]   Interfacial reactions between sapphire and Ag-Cu-Ti-based active braze alloys [J].
Ali, Majed ;
Knowles, Kevin M. ;
Mallinson, Phillip M. ;
Fernie, John A. .
ACTA MATERIALIA, 2016, 103 :859-869
[3]   Microstructural evolution and characterisation of interfacial phases in Al2O3/Ag-Cu-Ti/Al2O3 braze joints [J].
Ali, Majed ;
Knowles, Kevin M. ;
Mallinson, Phillip M. ;
Fernie, John A. .
ACTA MATERIALIA, 2015, 96 :143-158
[4]   Joining of SiO2 ceramic and TC4 alloy by nanoparticles modified brazing filler metal [J].
Bian, Hong ;
Song, Yanyu ;
Liu, Duo ;
Lei, Yuzhen ;
Song, Xiaoguo ;
Cao, Jian .
CHINESE JOURNAL OF AERONAUTICS, 2020, 33 (01) :383-390
[5]   Microstructure Evolution and Mechanical Properties of Titanium/Alumina Brazed Joints for Medical Implants [J].
Bian, Hong ;
Song, Xiaoguo ;
Hu, Shengpeng ;
Lei, Yuzhen ;
Jiao, Yide ;
Duan, Shutong ;
Feng, Jicai ;
Long, Weimin .
METALS, 2019, 9 (06)
[6]  
Blake T., 1993, Wettability
[7]   CONTACT ANGLES [J].
CASSIE, ABD .
DISCUSSIONS OF THE FARADAY SOCIETY, 1948, 3 :11-16
[8]  
Coudurier L., 1991, LECT NOTE PHYS, V386, P15
[9]   Microstructure and mechanical performance of composite joints of sapphire by ultrasonic-assisted brazing [J].
Cui Wei ;
Li Shuqi ;
Yan Jiuchun ;
Zhang Xing .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2018, 257 :1-6
[10]   Chemical reaction-limited spreading: the triple line velocity versus contact angle relation [J].
Dezellus, O ;
Hodaj, F ;
Eustathopoulos, N .
ACTA MATERIALIA, 2002, 50 (19) :4741-4753