Effects of static electric field on the fracture behavior of piezoelectric ceramics

The paper gives an overview on experimental observations of the failure behavior of electrically insulating and conducting cracks in piezoelectric ceramics. The experiments include the indentation fracture test, the bending test on smooth samples, and the fracture test on pre-notched (or pre-cracked) compact tension samples. For electrically insulating cracks, the experimental results show a complicated fracture behavior under electrical and mechanical loading. Fracture data are much scattered when a static electric field is applied. A statistically based fracture criterion is required. For electrically conducting cracks, the experimental results demonstrate that static electric fields can fracture poled and depoled lead zirconate titanate ceramics and that the concepts of fracture mechanics can be used to measure the electrical fracture toughness. Furthermore, the electrical fracture toughness is much higher than the mechanical fracture toughness. The highly electrical fracture toughness arises from the greater energy dissipation around the conductive crack tip under purely electric loading, which is impossible under mechanical loading in the brittle ceramics.