Compaction equations: a comparison of the Heckel and Kawakita equations

被引:259
作者
Denny, PJ [1 ]
机构
[1] Synetix Res & Technol, Billingham TS23 1LB, Cleveland, England
关键词
compaction equations; Heckel equation; Kawakita equation;
D O I
10.1016/S0032-5910(02)00111-0
中图分类号
TQ [化学工业];
学科分类号
0817 ;
摘要
The background and theoretical and experimental requirements of powder compaction equations have been briefly reviewed. There have been many equations proposed. However, the equations most commonly used today are the Heckel and Kawakita ones, because they alone have claimed to be able to relate to the physical properties of the materials being compacted. There has been much discussion about their relative merits, and in their form, they appear very different. The two equations are discussed in detail and examples are given, and their relative merits are discussed. However, it is first shown for applied pressures, which are low compared to the yield strength of the particles, that they are identical in form. It is then shown mathematically that if a pressure dependent term is used in the Heckel equation then the resulting modified equation is very similar to the Kawakita one and, in fact, becomes identical in form for a particular, likely value of the pressure dependency term. It is concluded that the Kawakita equation is a special case of the more general, modified Heckel equation. It is further concluded that compaction equations need further development to take into account the anisotropy in compacts made by uniaxial compaction. It is shown that the Poisson's ratio of compacts will also increase with applied pressure, and this must be considered. (C) 2002 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:162 / 172
页数:11
相关论文
共 42 条
[1]   Micromechanical analyses of the pressure-volume relationships for powders under confined uniaxial compression [J].
Adams, MJ ;
McKeown, R .
POWDER TECHNOLOGY, 1996, 88 (02) :155-163
[2]   AGGLOMERATE STRENGTH MEASUREMENT USING A UNIAXIAL CONFINED COMPRESSION TEST [J].
ADAMS, MJ ;
MULLIER, MA ;
SEVILLE, JPK .
POWDER TECHNOLOGY, 1994, 78 (01) :5-13
[3]   STUDIES ON DIRECT COMPRESSION OF TABLETS .10. MEASUREMENT OF TABLET SURFACE-AREA BY PERMEAMETRY [J].
ALDERBORN, G ;
DUBERG, M ;
NYSTROM, C .
POWDER TECHNOLOGY, 1985, 41 (01) :49-56
[4]  
ANDRIEVSKI RA, 1994, INT J POWDER METALL, V30, P59
[5]  
ARAKAWA M, 1965, J SOC MATER SCI JPN, V14, P764
[6]  
ARAKAWA M, 1966, J SOC MAT SCI JPN, V15, P151
[7]  
ARZT E, 1983, ACTA METALL, V30, P1982
[8]   DEFORMATION TRANSITIONS [J].
ATKINS, AG ;
MAI, YW .
JOURNAL OF MATERIALS SCIENCE, 1986, 21 (04) :1093-1110
[9]  
Bal'shin MY., 1938, VESTNIK METALLOPROM, V18, P124
[10]   COMPACTION OF PLASTIC POWDERS [J].
BAUMARD, JF ;
COUPELLE, P .
JOURNAL OF MATERIALS SCIENCE LETTERS, 1994, 13 (02) :93-95