Dynamic failure and adiabatic shearbands in fine-grain 93W-4.9Ni-2.1Fe alloy withY2O3 addition under lower high-strain-rate (HSR) compression

被引:37
作者
Fan, J. L. [1 ]
Gong, X. [1 ]
Huang, B. Y. [1 ]
Song, M. [1 ]
Liu, T. [1 ]
Qi, M. G. [1 ]
Tian, J. M. [1 ]
Li, S. K. [2 ]
机构
[1] Cent S Univ, State Key Lab Powder Met, Changsha 410083, Hunan, Peoples R China
[2] Beijing Inst Technol, Sch Mat Sci & Engn, Beijing 100081, Peoples R China
关键词
Tungsten heavy alloy; Fine-grain; Dynamic failure; Adiabatic shearbands; TUNGSTEN HEAVY ALLOY; COMPOSITE; MECHANISM; BEHAVIOR; IMPACT;
D O I
10.1016/j.mechmat.2009.08.006
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In this paper, Y2O3 dispersed 93W-4.9Ni-2.1Fe alloy with fine grains (FG) of about 3-5 mu m has been fabricated by liquid-phase sintering of their respective nanocomposite powders. The dynamic properties of FG-WHA have been investigated under uniaxial dynamic compression using Split Hopkinson Pressure Bar. The results show that the FG-WHA exhibits an almost ideal elastic-plastic behavior with no work hardening and susceptibility of the adiabatic shear localization at lower strain rates than the traditional WHA. Two obvious adiabatic shearbands have been observed at the strain rate of 1900 s(-1). The adiabatic shearbands origins in the crack tip region in the surface area of the specimen, propagating deeply into the specimen along orientations at 45 degrees to the impact direction. The bands have much narrower width of about 10-25 mu m than that for traditional WHA (the width of bands is about 200 mu m according to Kim et al. (1998a,b)). Within the center of the bands. the tungsten grains are severely elongated to be fibrous and orient along the propagation directions of the adiabatic shear bands. exhibiting plastic flow localized instability. (C) 2009 Elsevier Ltd. All rights reserved.
引用
收藏
页码:24 / 30
页数:7
相关论文
共 18 条
[1]  
ANDREW SP, 1991, TUNGSTEN AND TUNGSTEN ALLOYS : RECENT ADVANCES, P141
[2]   Preparation of fine grain tungsten heavy alloy with high properties by mechanical alloying and yttrium oxide addition [J].
Fan Jing-lian ;
Liu Tao ;
Cheng Hui-chao ;
Wang Deng-long .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2008, 208 (1-3) :463-469
[3]   Controlling factors for the brittle-to-ductile transition in tungsten single crystals [J].
Gumbsch, P ;
Riedle, J ;
Hartmaier, A ;
Fischmeister, HF .
SCIENCE, 1998, 282 (5392) :1293-1295
[4]   Microstructural study of adiabatic shear bands formed by high-speed impact in a tungsten heavy alloy penetrator [J].
Kim, DK ;
Lee, S ;
Baek, WH .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 249 (1-2) :197-205
[5]   Adiabatic shearband in WHA in high-strain-rate compression [J].
Kim, DS ;
Nemat-Nasser, S ;
Isaacs, JB ;
Lischer, D .
MECHANICS OF MATERIALS, 1998, 28 (1-4) :227-236
[6]  
LANDFORD J, 1991, TUNGSTEN TUNGSTEN AL, P151
[7]  
Lassner Erik., 1999, TUNGSTEN-SINGAPORE, P85
[8]   Thermal softening of a particle-modified tungsten-based composite under adiabatic compression [J].
Leduc, PR ;
Bao, G .
INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 1997, 34 (13) :1563-1581
[9]   The strain rate and temperature dependence of the dynamic impact response of tungsten composite [J].
Lee, WS ;
Xiea, GL ;
Lin, CF .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 257 (02) :256-267
[10]  
[李英雷 Li Yinglei], 2003, [兵工学报, Acta Armamentarii], V24, P378