Influence of the Casting Conditions on the Structure and Properties of a Co-Cr-Mo Dental Alloy

被引：0

作者：

Vitalariu, Anca ^{[1
]}

Leata, Razvan ^{[2
]}

Chelariu, Romeu ^{[3
]}

Munteanu, Corneliu ^{[3
]}

Cimpoesu, Ramona ^{[3
]}

Ilie, Mariana ^{[2
]}

Comaneci, Radu ^{[3
]}

Moisei, Mihaela ^{[2
]}

机构：

[1] Gr T Popa Univ Med & Pharm, Iasi 700115, Romania

[2] Dunarea de Jos Univ Galati, Fac Med & Pharm, Galati 800008, Romania

[3] Gheorghe Asachi Tech Univ Iasi, Iasi 700050, Romania

来源：

REVISTA DE CHIMIE | 2015年 / 66卷 / 12期

关键词：

Co-Cr-Mo dental alloy; casting; mold temperature; corrosion; artificial saliva; MECHANICAL-PROPERTIES; BEHAVIOR; BIOCOMPATIBILITY;

D O I：

暂无

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

The paper aims to investigate the influence of the casting conditions and in particular of the mold temperature (T-mold) - as the main parameter of the solidification process - on structure, corrosion resistance and mechanical properties of a Co-Cr-Mo dental alloy. The alloy has been cast at T-mold = 500 and 900 degrees C and the solidification structure has been investigated by using optical and scanning electron microscopy (SEM). Corrosion of the as-cast alloy in two different artificial salivas having pH = 6.0 and 7.7, and mechanical testing revealed that casting Co-Cr-Mo dental alloy at lowest permissible temperature (500 degrees C) does not adversely affect the structure and properties of the alloy. Due to the highest melt solidification rate, an improvement in structure and corrosion resistance while maintaining the mechanical properties was found.

引用

页码：2147 / 2151

页数：5

共 50 条

[21] Nd:YAG laser cladding of Co-Cr-Mo alloy on γ-TiAl substrate
Barekat, Masoud
Razavi, Reza Shoja
Ghasemi, Ali
OPTICS AND LASER TECHNOLOGY, 2016, 80 : 145 - 152
[22] Modification of mechanical properties of sintered implant materials on the base of Co-Cr-Mo alloy
Gradzka-Dahlke, M.
Dabrowski, J. R.
Dabrowski, B.
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2008, 204 (1-3) : 199 - 205
[23] Enhancement of the corrosion properties of selective laser melted Co-Cr-Mo alloy by selective oxidation annealing
Im, Hyeon-Tae
Kim, Dae Ha
Seo, Bosung
Park, Jae-Young
Park, Ki Beom
Lee, Da Hye
Mo, Chan Bin
Kim, Young Do
Park, Kwangsuk
Park, Hyung-Ki
MATERIALS CHARACTERIZATION, 2023, 195
[24] Analysis of Microstructure Evolution of Co-Cr-Mo Alloy during Isothermal Forging
Gamin, Yury V.
Skugorev, Alexander V.
Karashaev, Mukhamed M.
Kin, Tatiana Y.
Galkin, Sergei P.
Mahmoud Alhaj Ali, Abdullah
Cheverikin, Vladimir V.
METALS, 2023, 13 (09)
[25] A Comparative Analysis of the Corrosive Effect of Artificial Saliva of Variable pH on DMLS and Cast Co-Cr-Mo Dental Alloy
Puskar, Tatjana
Jevremovic, Danimir
Williams, Robert J.
Eggbeer, Dominic
Vukelic, Djordje
Budak, Igor
MATERIALS, 2014, 7 (09) : 6486 - 6501
[26] Defects-tolerant Co-Cr-Mo dental alloys prepared by selective laser melting.
Qian, B.
Saeidi, K.
Kvetkova, L.
Lofaj, F.
Xiao, C.
Shen, Z.
DENTAL MATERIALS, 2015, 31 (12) : 1435 - 1444
[27] Prediction of influence of Co-Cr-Mo alloy coating on the wear rate of aluminium with HCl solution
Reddy, Pratapa Y.
Narayana, Lakshmi K.
Mallik, M. Kedar
MATERIALS TODAY-PROCEEDINGS, 2021, 42 : 1287 - 1296
[28] In vitro biocorrosion of Co-Cr-Mo implant alloy by macrophage cells
Lin, HY
Bumgardner, JD
JOURNAL OF ORTHOPAEDIC RESEARCH, 2004, 22 (06) : 1231 - 1236
[29] Fatigue strength of Co-Cr-Mo alloy clasps prepared by selective laser melting
Kajima, Yuka
Takaichi, Atsushi
Nakamoto, Takayuki
Kimura, Takahiro
Yogo, Yoshiaki
Ashida, Maki
Doi, Hisashi
Nomura, Naoyuki
Takahashi, Hidekazu
Hanawa, Takao
Wakabayashi, Noriyuki
JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS, 2016, 59 : 446 - 458
[30] Cytocompatibility for Co-Cr-Mo alloy with a small amount of zirconium or carbon
Numata, Yasuko
Syuto, Bunei
Nomura, Naoyuki
Chiba, Akihiko
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2007, 71 (07) : 578 - 585

← 1 2 3 4 5 →