Leaching of valuable metals from electric arc furnace dust-Tetrabromobisphenol A pyrolysis residues

被引:34
作者
Al-Harahsheh, Mohammad [1 ]
Aljarrah, Mohannad [1 ]
Rummanah, Fahed [1 ]
Abdel-Latif, Kameel [1 ]
Kingman, Sam [2 ]
机构
[1] Jordan Univ Sci & Technol, Chem Engn Dept, Irbid 22110, Jordan
[2] Univ Nottingham, Fac Engn, Nottingham NG7 2RD, England
关键词
Pyrolysis; EAFD; TBBPA; Leaching; Lead; Zinc; Iron; Bromide; BROMINATED FLAME RETARDANTS; DILUTED SULFURIC-ACID; EAF DUST; THERMAL-DECOMPOSITION; PLASTIC WASTE; OXIDE; ZINC; DEGRADATION; ATMOSPHERES; EXTRACTION;
D O I
10.1016/j.jaap.2017.04.019
中图分类号
O65 [分析化学];
学科分类号
070302 ; 081704 ;
摘要
Pyrolysis of electric arc furnace dust (EAFD) mixed with Tetrabromobisphenol A (TBBPA) was performed in an inert atmosphere in order to extract valuable metals. Several pyrolysis variables were investigated in this work including pyrolysis temperature, EAFD:TBBPA ratio, and final pyrolysis temperature. The pyrolysis residue was subjected to leaching in water under variable conditions (pH and use of oxidizing agent). The HBr released during decomposition of TBBPA was found to react with the metal oxides present in the EAFD. It was found that pyrolysis above 350 degrees C caused appreciable vaporization of lead and zinc bromides. Upon leaching of the pyrolysis residue it was found that almost all of the Pb present could be recovered at a low pH, whilst an increase in solution pH led to the precipitation of Pb in the form of Pb(OH)Br. It was also found that about 91% of Zinc could be recovered, but zinc recovery was less sensitive to pH when compared to Pb suggesting the possibility of their separation. Most importantly, it was found that iron remained mostly in the solid precipitate after leaching at a pH > 3, while the use of H2O2 as an oxidizing agent resulted in the precipitation of iron at pH lower than 3.
引用
收藏
页码:50 / 60
页数:11
相关论文
共 37 条
[1]   Pyrolysis of poly(vinyl chloride) and-electric arc furnacedust mixtures [J].
Al-Harahsheh, Mohammad ;
Al-Otoom, Awni ;
Al-Makhadmah, Leema ;
Hamilton, Ian E. ;
Kingman, Sam ;
Al-Asheh, Sameer ;
Hararah, Muhanned .
JOURNAL OF HAZARDOUS MATERIALS, 2015, 299 :425-436
[2]   Microwave treatment of electric arc furnace dust with PVC: Dielectric characterization and pyrolysis-leaching [J].
Al-harahsheh, Mohammad ;
Kingman, Sam ;
Al-Makhadmah, Leema ;
Hamilton, Ian E. .
JOURNAL OF HAZARDOUS MATERIALS, 2014, 274 :87-97
[3]   Thermal Recycling of Brominated Flame Retardants with Fe2O3 [J].
Altarawneh, Mohammednoor ;
Ahmed, Oday H. ;
Jiang, Zhong-Tao ;
Dlugogorski, Bogdan Z. .
JOURNAL OF PHYSICAL CHEMISTRY A, 2016, 120 (30) :6039-6047
[4]   Mechanism of Thermal Decomposition of Tetrabromobisphenol A (TBBA) [J].
Altarawneh, Mohammednoor ;
Dlugogorski, Bogdan Z. .
JOURNAL OF PHYSICAL CHEMISTRY A, 2014, 118 (40) :9338-9346
[5]   Investigation of potential uses of electric-arc furnace dust (EAFD) in concrete [J].
AlZaid, RZ ;
AlSugair, FH ;
AlNegheimish, AI .
CEMENT AND CONCRETE RESEARCH, 1997, 27 (02) :267-278
[6]  
Balk D.S., 2000, MIN PROC EXT MET REV, V109, P121
[7]   The selective alkaline leaching of zinc oxide from Electric Arc Furnace dust pre-treated with calcium oxide [J].
Chairaksa-Fujimoto, Romchat ;
Maruyama, Katsuya ;
Miki, Takahiro ;
Nagasaka, Tetsuya .
HYDROMETALLURGY, 2016, 159 :120-125
[8]  
Clariant, 2013, FLAM RET MARK
[9]   Alkaline leaching of zinc from electric arc furnace steel dust [J].
Dutra, AJB ;
Paiva, PRP ;
Tavares, LM .
MINERALS ENGINEERING, 2006, 19 (05) :478-485
[10]   Study on simultaneous recycling of EAF dust and plastic waste containing TBBPA [J].
Grabda, Mariusz ;
Oleszek, Sylwia ;
Shibata, Etsuro ;
Nakamura, Takashi .
JOURNAL OF HAZARDOUS MATERIALS, 2014, 278 :25-33