Processing of titanium foams using magnesium spacer particles

被引：194

作者：

Esen, Z. ^{[1
]}

Bor, S. ^{[1
]}

机构：

[1] Middle E Tech Univ, Dept Met & Mat Engn, TR-06531 Ankara, Turkey

来源：

SCRIPTA MATERIALIA | 2007年 / 56卷 / 05期

关键词：

titanium; magnesium; foam; sintering; mechanical property;

D O I：

10.1016/j.scriptamat.2006.11.010

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Production of titanium foams using magnesium powders as spacer particles has been investigated. Titanium foams having porosities in the range 45-70% with an average pore size of around 525 mu m have been manufactured. The resultant yield strength and elastic moduli values were observed to vary in the range 15-116 MPa and 0.42-8.8 GPa, respectively. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

引用

页码：341 / 344

页数：4

共 14 条

[1] Manufacture, characterisation and application of cellular metals and metal foams
Banhart, J
[J]. PROGRESS IN MATERIALS SCIENCE, 2001, 46 (06) : 559 - U3
[2] HATTIANGADI A, 2000, J AM CERAM SOC, V11, P83
[3] Preparation of high porosity metal foams
Jee, CSY
Özgüven, N
Guo, ZX
Evans, JRG
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2000, 31 (06): : 1345 - 1352
[4] Lorna J.Gibson., 1999, CELLULAR SOLIDS STRU
[5] Microstructure evolution during solid-state foaming of titanium
Murray, NGD
Dunand, DC
[J]. COMPOSITES SCIENCE AND TECHNOLOGY, 2003, 63 (16) : 2311 - 2316
[6] Microstructures and mechanical properties of porous titanium compacts prepared by powder sintering
Oh, IH
Nomura, N
Hanada, S
[J]. MATERIALS TRANSACTIONS, 2002, 43 (03) : 443 - 446
[7] Pilliar RM, 1998, INT J POWDER METALL, V34, P33
[8] Ricceri R, 2003, INT J POWDER METALL, V39, P53
[9] Comparison of physical property porosity behaviour with minimum solid area models
Rice, RW
[J]. JOURNAL OF MATERIALS SCIENCE, 1996, 31 (06) : 1509 - 1528
[10] Evaluation and extension of physical property-porosity models based on minimum solid area
Rice, RW
[J]. JOURNAL OF MATERIALS SCIENCE, 1996, 31 (01) : 102 - 118

← 1 2 →