Surface tension and thermodynamic properties of liquid Ag-Bi solutions

With the maximum bubble pressure method, the density and surface tension were measured for five Ag-Bi liquid alloys (X-Bi = 0.05, 0.15, 0.25, 0.5, and 0.75), as well as for pure silver. The experiments were performed in the temperature range 544-1443 K. Linear dependences of both density and surface tension versus temperature were observed, and therefore the experimental data were described by linear equations. The density dependence on concentration and temperature was derived using the polynomial method. A similar dependence of surface tension on temperature and concentration is presented. Next, the Gibbs energy of formation of solid Bi2O3, as well as activities of Bi in liquid Ag-Bi alloys, were determined by a solid-state electromotive force (emf) technique using the following galvanic cells: Ni, NiO, Pt/O-2/W, AgxBi(1-x Bi2O3(s). The Gibbs energy of formation of solid Bi2O3 from pure elements was derived: DeltaG(f(alpha-Bi2O3))(o) = -598 148 + 309.27T [J . mol(-1)] and DeltaG(f(delta-Bi2O3))(o) = -548 009 + 258.94T [J . mol(-1)]; the temperature and the heat of the alpha --> delta transformation for this solid oxide were calculated as 996 K and 50.14 J . mol(-1). Activities of Bi in the liquid alloys were determined in the temperature range from 860-1075 K, for five Ag-Bi alloys (X-Ag = 0.2, 0.35, 0.5, 0.65, 0.8), and a Redlich-Kister polynomial expansion was used to describe the thermodynamic properties of the liquid phase. Using Thermo-Calc software, the Ag-Bi phase diagram was calculated. Finally, thermodynamic data were used to predict surface tension behavior in the Ag-Bi binary system.