Flame Retarded Rigid Polyurethane Foams Composites Modified by Aluminum Diethylphosphinate and Expanded Graphite

被引:19
作者
Hu, Yuxiang [1 ]
Zhou, Zijian [2 ]
Li, Shuisheng [1 ]
Yang, Dong [1 ]
Zhang, Shui [1 ]
Hou, Yakang [1 ]
机构
[1] China Construct Fifth Engn Div Co Ltd, Changsha, Peoples R China
[2] Anhui Univ Technol, Sch Architecture & Civil Engn, Maanshan, Peoples R China
关键词
flame retarded; rigid polyurethane foams; aluminum diethylphosphinate; expanded graphite; thermal stability; THERMAL-DEGRADATION; BLACK PHOSPHORUS; STRATEGY; CONSTRUCTION; SUPPRESSION;
D O I
10.3389/fmats.2020.629284
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Rigid polyurethane foam (RPUF) was an organic porous material, which was applied in many fields for excellent thermal insulation and mechanical properties, especially in building insulation. However, the poor fire performance significantly suppresses its further application. In this work, aluminum diethylphosphinate (ADP) combined with expanded graphite (EG) to form a synergistic flame retarded system, which was introduced to fabricate flame retarded rigid polyurethane foam composites (FR-RPUF) by one-step water-blown method. Furthermore, thermal insulation, thermal stability, fire performance, and decomposition products of RPUF and FR-RPUF composites were systematically investigated. It was found that FR-RPUF composites possessed LOI of 25.9 vol% with V-1 rating in UL-94 test when 10 php of ADP and 20 php of EG were added, which were better than RPUF composites with ADP or EG added alone. MCC test showed that RPUF/ADP24/EG6 had the lowest PHRR value of 159.85 W/g, which was 52.01 W/g lower than that of pure RPUF. Gas phase products investigation implied that the combination of ADP and EG could decrease toxic and combustible gases intensities, thus significantly enhancing fire safety of FR-RPUF composites. SEM test indicated that ADP and EG promoted the formation of dense and continuous char residue, which significantly inhibited heat and substance transfer in combustion, thus significantly enhancing fire performance of FR-RPUF composites.
引用
收藏
页数:11
相关论文
共 36 条
[1]   Synergistic effect of expandable graphite and phenylphosphonic-aniline salt on flame retardancy of rigid polyurethane foam [J].
Acuna, Pablo ;
Lin, Xuebao ;
Santiago Calvo, Mercedes ;
Shao, Zhubao ;
Perez, Nerea ;
Villafane, Fernando ;
Angel Rodriguez-Perez, Miguel ;
Wang, De-Yi .
POLYMER DEGRADATION AND STABILITY, 2020, 179
[2]   Synergistic effects of expandable graphite and ammonium pentaborate octahydrate on the flame-retardant, thermal insulation, and mechanical properties of rigid polyurethane foam [J].
Akdogan, Emre ;
Erdem, Murat ;
Ureyen, Mustafa Erdem ;
Kaya, Metin .
POLYMER COMPOSITES, 2020, 41 (05) :1749-1762
[3]   Fatigue properties of highly oriented polypropylene tapes and all-polypropylene composites [J].
Barkoula, N. -M. ;
Alcock, B. ;
Cabrera, N. O. ;
Peijs, T. .
POLYMERS & POLYMER COMPOSITES, 2008, 16 (02) :101-113
[4]   Castor-oil derived nonhalogenated reactive flame-retardant-based polyurethane foams with significant reduced heat release rate [J].
Bhoyate, Sanket ;
Ionescu, Mihail ;
Kahol, Pawan K. ;
Gupta, Ram K. .
JOURNAL OF APPLIED POLYMER SCIENCE, 2019, 136 (13)
[5]   The Synergistic Effect of Ionic Liquid-Modified Expandable Graphite and Intumescent Flame-Retardant on Flame-Retardant Rigid Polyurethane Foams [J].
Chen, Yongjun ;
Luo, Yuanfang ;
Guo, Xiaohui ;
Chen, Lijuan ;
Jia, Demin .
MATERIALS, 2020, 13 (14)
[6]   Structure and Flame-Retardant Actions of Rigid Polyurethane Foams with Expandable Graphite [J].
Chen, Yongjun ;
Luo, Yuanfang ;
Guo, Xiaohui ;
Chen, Lijuan ;
Xu, Tiwen ;
Jia, Demin .
POLYMERS, 2019, 11 (04)
[7]   Effects of ammonium polyphosphate microencapsulated on flame retardant and mechanical properties of the rigid polyurethane foam [J].
Cheng, Jiaji ;
Niu, Shaoshuai ;
Ma, Dan ;
Zhou, Yue ;
Zhang, Feng ;
Qu, Wenjuan ;
Wang, Dong ;
Li, Shaoxiang ;
Zhang, Xinlong ;
Chen, Xianqun .
JOURNAL OF APPLIED POLYMER SCIENCE, 2020, 137 (48)
[8]   Hierarchical core-shell TiO2@LDH@Ni(OH)2 architecture with regularly-oriented nanocatalyst shells: Towards improving the mechanical performance, flame retardancy and toxic smoke suppression of unsaturated polyester resin [J].
Chu, Fukai ;
Xu, Zhoumei ;
Zhou, Yifan ;
Zhang, Shenghe ;
Mu, Xiaowei ;
Wang, Junling ;
Hu, Weizhao ;
Song, Lei .
CHEMICAL ENGINEERING JOURNAL, 2021, 405
[9]   A facile strategy to simultaneously improve the mechanical and fire safety properties of ramie fabric-reinforced unsaturated polyester resin composites [J].
Chu, Fukai ;
Yu, Xiaojuan ;
Hou, Yanbei ;
Mu, Xiaowei ;
Song, Lei ;
Hu, Weizhao .
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2018, 115 :264-273
[10]   Construction of Hierarchical Natural Fabric Surface Structure Based on Two-Dimensional Boron Nitride Nanosheets and Its Application for Preparing Biobased Toughened Unsaturated Polyester Resin Composites [J].
Chu, Fukai ;
Zhang, Dichang ;
Hou, Yanbei ;
Qiu, Shuilai ;
Wang, Junling ;
Hu, Weizhao ;
Song, Lei .
ACS APPLIED MATERIALS & INTERFACES, 2018, 10 (46) :40168-40179