Mechanical behavior of Al-Li/SiC composites: Part II. Cyclic deformation

被引:9
作者
Poza, P [1 ]
Llorca, J [1 ]
机构
[1] Univ Politecn Madrid, Dept Mat Sci, E-28040 Madrid, Spain
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1999年 / 30卷 / 03期
关键词
D O I
10.1007/s11661-999-0079-8
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The deformation and failure mechanisms under cyclic deformation in an 8090 Al-Li alloy reinforced with 15 vol pct SiC particles were studied and compared to those of the unreinforced alloy. The materials were tested under fully reversed cyclic deformation in the peak-aged and naturally aged conditions to obtain the cyclic response and the cyclic stress-strain curve. The peak-aged materials remained stable or showed slight cyclic softening, and the deformation mechanisms were not modified by the presence of the ceramic reinforcements: dislocations were trapped by the S ' precipitates and the stable response was produced by the mobile dislocations shuttling between the precipitates to accommodate the plastic strain without further hardening. The naturally aged materials exhibited cyclic hardening until failure, which was attributed to the interactions among dislocations. Strain localization and slip-band formation were observed in the naturally aged alloy at high cyclic strain amplitudes, whereas the corresponding composite presented homogeneous deformation. Fracture was initiated by grain-boundary delamination in the unreinforced materials, while progressive reinforcement fracture under cyclic deformation was the main damage mechanism in the composites. The influence of these deformation and damage processes in low-cycle fatigue life is discussed.
引用
收藏
页码:857 / 866
页数:10
相关论文
共 28 条
[1]  
ALLISON JE, FUNDAMENTALS METAL M, P269
[2]   FATIGUE BEHAVIOR OF A 2XXX SERIES ALUMINUM-ALLOY REINFORCED WITH 15 VOL PCT SICP [J].
BONNEN, JJ ;
ALLISON, JE ;
JONES, JW .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (05) :1007-1019
[3]  
CALABRESE C, 1974, MATER SCI ENG, V13, P141, DOI 10.1016/0025-5416(74)90183-9
[4]   MICROSTRUCTURE AND MECHANICAL-PROPERTIES OF MECHANICALLY ALLOYED, INGOT METALLURGY AND POWDER-METALLURGY AL-LI-CU-MG ALLOYS [J].
CHEN, RT ;
STARKE, EA .
MATERIALS SCIENCE AND ENGINEERING, 1984, 67 (02) :229-245
[5]   THE EFFECT OF MINOR ALLOYING ELEMENTS ON THE MECHANICAL-PROPERTIES OF AL-CU-LI ALLOYS [J].
FENG, WX ;
LIN, FS ;
STARKE, EA .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1984, 15 (06) :1209-1220
[6]   PARTICLE-SIZE, VOLUME FRACTION AND MATRIX STRENGTH EFFECTS ON FATIGUE BEHAVIOR AND PARTICLE FRACTURE IN 2124 ALUMINUM-SICP COMPOSITES [J].
HALL, JN ;
JONES, JW ;
SACHDEV, AK .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1994, 183 (1-2) :69-80
[7]   THE INFLUENCE OF AGING ON FATIGUE CRACK-GROWTH IN SIC-PARTICULATE REINFORCED 8090 [J].
KNOWLES, DM ;
KING, JE .
ACTA METALLURGICA ET MATERIALIA, 1991, 39 (05) :793-806
[8]   FRACTURE ALONG PLANAR SLIP BANDS [J].
KOSS, DA ;
CHAN, KS .
ACTA METALLURGICA, 1980, 28 (09) :1245-1252
[9]   INFLUENCE OF REINFORCEMENT FRACTURE ON THE CYCLIC STRESS-STRAIN CURVE OF METAL-MATRIX COMPOSITES [J].
LLORCA, J ;
POZA, P .
ACTA METALLURGICA ET MATERIALIA, 1995, 43 (11) :3959-3969
[10]   THE CYCLIC STRESS-STRAIN CURVE OF DISCONTINUOUSLY-REINFORCED AL-BASED AND MG-BASED COMPOSITES [J].
LLORCA, J .
SCRIPTA METALLURGICA ET MATERIALIA, 1994, 30 (06) :755-760